Fatigue cracking possibility along grain boundaries and persistent slip bands in copper bicrystals

IMR OpenIR

	Fatigue cracking possibility along grain boundaries and persistent slip bands in copper bicrystals
	Z. F. Zhang; Z. G. Wang; S. X. Li
	1998
发表期刊	Fatigue & Fracture of Engineering Materials & Structures
ISSN	8756-758X
卷号	21 期号:11 页码:1307-1316
摘要	In this paper, the fatigue cracking possibility in different kinds of copper bicrystals with large-angle grain boundaries (GBs) and copper multicrystals containing some low-angle GBs are compared. The results showed that the fatigue cracks, in the copper bicrystals, always nucleated firstly along GBs no matter whether the GBs are perpendicular or parallel to the stress axis. Whereas, for the copper multicrystals containing low-angle GBs, the persistent slip bands (PSBs) are always the preferential sites to initiate fatigue cracks no matter whether low-angle GBs are perpendicular or parallel to the stress axis. Additionally, the fatigue lives of the GBs, and the [(1) over bar 23] and [(3) over bar 35] grains in the [(1) over bar 23] perpendicular to [(3) over bar 35] and [(5) over bar 913] perpendicular to [(5) over bar 79] bicrystals were measured at different cyclic stresses and strain amplitudes. The results show that intergranular fracture always occurred prior to transgranular Fracture in those bicrystals. The fatigue lives increased in the order of the GB, the [(1) over bar 23] and the [(3) over bar 35] grains in the [(1) over bar 23] perpendicular to [(3) over bar 35] bicrystal under cyclic tension-tension loading. On the other hand, the fatigue life of the GB in the [(5) over bar 913] perpendicular to [(5) over bar 79] bicrystal is about two to three times higher than that in the [(1) over bar 23] perpendicular to [(3) over bar 35] bicrystal. Based on these experimental results from the copper bicrystals and multicrystals, it is indicated that the possibility of fatigue cracking increased in the order of low-angle GBs, PSBs and large-angle GBs. It is suggested that both the PSB-GB mechanism and the step mechanism required for GB fatigue cracking were questionable, and the interaction modes of PSBs with GBs may be more important for intergranular fatigue cracking.
部门归属	chinese acad sci, inst met res, state key lab fatigue & fracture mat, shenyang 110015, peoples r china.;zhang, zf (reprint author), chinese acad sci, inst met res, state key lab fatigue & fracture mat, shenyang 110015, peoples r china
关键词	Fatigue Cracking Fatigue Lives Large-angle Gbs Low-angle Gbs Psbs Electron Channeling Contrast Low Amplitude Fatigue Stage-i Propagation High Strain Fatigue Cyclic Deformation Single-crystals Initiation Nucleation Metals Growth
URL	查看原文
WOS记录号	WOS:000077863300003
引用统计	被引频次：25[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/37891
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Z. F. Zhang,Z. G. Wang,S. X. Li. Fatigue cracking possibility along grain boundaries and persistent slip bands in copper bicrystals[J]. Fatigue & Fracture of Engineering Materials & Structures,1998,21(11):1307-1316.
APA	Z. F. Zhang,Z. G. Wang,&S. X. Li.(1998).Fatigue cracking possibility along grain boundaries and persistent slip bands in copper bicrystals.Fatigue & Fracture of Engineering Materials & Structures,21(11),1307-1316.
MLA	Z. F. Zhang,et al."Fatigue cracking possibility along grain boundaries and persistent slip bands in copper bicrystals".Fatigue & Fracture of Engineering Materials & Structures 21.11(1998):1307-1316.