	Oxidation behavior of Fe26Cr1Mo stainless steel in the presence of Ni-La2O3 electrodeposited composite film
	X. Peng; L. J. Zhou; T. F. Li; W. T. Wu
	1997
发表期刊	Journal of Rare Earths
ISSN	1002-0721
卷号	15 期号:3 页码:195-200
摘要	The oxidation behaviors of Fe26Cr1Mo with and without the Ni-La2O3 electrodeposited composite film have been investigated by thermogravimetric analysis (TGA) and a scanning electron microscope equipped with an energy-dispersive analytical X-ray system (SEM/EDAX). The experimental results show that the oxide scale growing on Fe26Cr1Mo exposed at 900 degrees C spalled severely during cooling, while after the stainless steel was coated with the Ni-La2O3 electrodeposited composite film, its high temperature cyclic oxidation resistance was significantly improved. The reason is that a La2O3-modified NiO scale, which has a superior adhesion to the substrate, was formed on the Fe26Cr1Mo stainless steel coated with Ni-La2O3 composite film.
部门归属	acad sinica,inst corros & protect met,state key lab corros & protect,shenyang 110015,peoples r china.
关键词	Rare Earths La Ni-la2o3 Electrodeposited Composite Film Stainless Steel Oxidation Behavior Scales
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/38062
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	X. Peng,L. J. Zhou,T. F. Li,et al. Oxidation behavior of Fe26Cr1Mo stainless steel in the presence of Ni-La2O3 electrodeposited composite film[J]. Journal of Rare Earths,1997,15(3):195-200.
APA	X. Peng,L. J. Zhou,T. F. Li,&W. T. Wu.(1997).Oxidation behavior of Fe26Cr1Mo stainless steel in the presence of Ni-La2O3 electrodeposited composite film.Journal of Rare Earths,15(3),195-200.
MLA	X. Peng,et al."Oxidation behavior of Fe26Cr1Mo stainless steel in the presence of Ni-La2O3 electrodeposited composite film".Journal of Rare Earths 15.3(1997):195-200.