Hydrogen-induced embrittlement wear of a high-strength, low-alloy steel in an acidic environment

IMR OpenIR

	Hydrogen-induced embrittlement wear of a high-strength, low-alloy steel in an acidic environment
	T. C. Zhang; X. X. Jiang; S. Z. Li
	1997
发表期刊	Corrosion
ISSN	0010-9312
卷号	53 期号:3 页码:200-205
摘要	Corrosive wear of a high-strength, low-alloy steel (HSLA) was examined in 0.02 mol/L sulfuric acid (H2SO4) solution at different polarized potentials and loads using a pin-on-disc wear device and a potentiostat. Morphologies of the wear tracks were observed by scanning electron microscopy (SEM). Hydrogen content in the surface or subsurface of wear tracks was determined using secondary ion mass spectrometry (SIMS). Results showed the increased material removal with a negative shift of potential in the cathodically polarized range resulted from the synergistic effect of hydrogen-induced damage and mechanical wear from hydrogen evolution on the wear surface. Increases in wear loss with potential in the anodically polarized range resulted from synergism between anodic dissolution and wear.
部门归属	acad sinica,inst met res,shenyang 110015,peoples r china.;zhang, tc (reprint author), univ sci & technol beijing,dept mat phys,beijing 100083,peoples r china
关键词	Corrosive Wear Embrittlement High-strength Low-alloy Steel Hydrogen-induced Damage Morphology Scanning Electron Microscopy Secondary Ion Mass Spectrometry Corrosive Wear Cracking
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/38211
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	T. C. Zhang,X. X. Jiang,S. Z. Li. Hydrogen-induced embrittlement wear of a high-strength, low-alloy steel in an acidic environment[J]. Corrosion,1997,53(3):200-205.
APA	T. C. Zhang,X. X. Jiang,&S. Z. Li.(1997).Hydrogen-induced embrittlement wear of a high-strength, low-alloy steel in an acidic environment.Corrosion,53(3),200-205.
MLA	T. C. Zhang,et al."Hydrogen-induced embrittlement wear of a high-strength, low-alloy steel in an acidic environment".Corrosion 53.3(1997):200-205.