Diffusion bonding of Ti3Al base alloy

IMR OpenIR

	Diffusion bonding of Ti3Al base alloy
	Y. Guo; J. M. Zhu; Z. J. He; P. Lian; Q. Wu; H. Zhang
	1996
发表期刊	Journal of Materials Science & Technology
ISSN	1005-0302
卷号	12 期号:6 页码:467-469
摘要	The effects of diffusion bonding temperature and holding time on the joint strength of Ti3Al base alloy has been investigated in this paper. The shear strength of Ti-14Al-21Nb-3Mo-V alloy diffusion bonding joint under pressure of 12 MPa at 990 degrees C for 70 min was obtained to 797.6 MPa which approaches the base material strength. In addition, a short-time diffusion bonding process was studied in order to decrease the bonding cost. With the deformation of the specimens of 2.5% and the bonding temperature of 990 degrees C for 15 min, the bonding strength could reach 801 MPa.
部门归属	weihai univ,weihai 260000,peoples r china.;guo, y (reprint author), acad sinica,inst met res,shenyang 110015,peoples r china
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/38286
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Y. Guo,J. M. Zhu,Z. J. He,et al. Diffusion bonding of Ti3Al base alloy[J]. Journal of Materials Science & Technology,1996,12(6):467-469.
APA	Y. Guo,J. M. Zhu,Z. J. He,P. Lian,Q. Wu,&H. Zhang.(1996).Diffusion bonding of Ti3Al base alloy.Journal of Materials Science & Technology,12(6),467-469.
MLA	Y. Guo,et al."Diffusion bonding of Ti3Al base alloy".Journal of Materials Science & Technology 12.6(1996):467-469.