Nanocomposite of Al95In5 synthesized by ball milling

IMR OpenIR

	Nanocomposite of Al95In5 synthesized by ball milling
	H. W. Sheng; J. Xu; X. K. Sun; K. Lu; Z. Q. Hu
	1995
发表期刊	Nanostructured Materials
ISSN	0965-9773
卷号	6 期号:1-4 页码:417-420
摘要	The microstructural evolution of Al95In5 powder mixture during ball milling is investigated using XRD, TEM, SEM EDX etc. It is shown that a nanocomposite of Al95In5 is formed after milling for 300 h. In the final milled product, the refined fn particles are embedded dispersively in the Al matrix and the grain sizes of Al and In reach 20 nm and 18 nm, respectively. Due to the partial fusion of the In component during milling, the conventional layered microstructure is not formed in the milled powders. The addition of In has a hindering effect on the grain refinement of the Al component. As tin impurity, Fe is dissolved in the Al matrix during milling, with a content of 0.87 at.% Fe after milling for 300 h, which results in a reduction of the lattice parameter of Al.
部门归属	sheng, hw (reprint author), acad sinica,inst met res,natl key lab rsa,shenyang 110015,peoples r china
关键词	Nanocrystalline
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/38663
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	H. W. Sheng,J. Xu,X. K. Sun,et al. Nanocomposite of Al95In5 synthesized by ball milling[J]. Nanostructured Materials,1995,6(1-4):417-420.
APA	H. W. Sheng,J. Xu,X. K. Sun,K. Lu,&Z. Q. Hu.(1995).Nanocomposite of Al95In5 synthesized by ball milling.Nanostructured Materials,6(1-4),417-420.
MLA	H. W. Sheng,et al."Nanocomposite of Al95In5 synthesized by ball milling".Nanostructured Materials 6.1-4(1995):417-420.