| CORROSION BEHAVIOR OF 8090 AL-LI ALLOY | |
| Z. Q. Hu; Y. Zhang; Y. L. Liu; Z. Y. Zhu | |
| 1993 | |
| Source Publication | Corrosion
 |
| ISSN | 0010-9312 |
| Volume | 49Issue:6Pages:491-498 |
| Abstract | An evaluation was conducted of the corrosion behavior of 8090 aluminum-lithium (Al-Li) alloy (UNS A98090), when aged under various conditions and subjected to corrosion in a solution of 3.5% NaCl + 1% H2O2. Susceptibility to pitting, intergranular corrosion, and exfoliation corrosion was shown to be influenced by heat treatment, which reduced from natural aging, through overaging to peak aging. Materials with peak aging showed low corrosion resistance. The decreased corrosion resistance corresponded to decreased corrosion potential of the alloy. Insoluble constituents were susceptible to corrosion. The corrosion extended along grain boundaries. Al-Li alloys showed mismatched tensile strength and stress corrosion resistance. The growth rate of stress corrosion cracks was large in the peak-aged state. The growth rate was strengthed by overaging, but tensile strength was reduced. That problem was solved by retrogression and reaging processing. |
| description.department | acad sinica,inst corros & protect met,shenyang 110015,peoples r china.;hu, zq (reprint author), acad sinica,inst met res,72 wenhua rd,shenyang 110015,peoples r china |
| Keyword | Aluminum-lithium Alloy Corrosion Resistance Exfoliation Corrosion Intergranular Corrosion Retrogression And Reaging Treatment Stress Corrosion Cracking Aluminum-alloy Strength Lithium |
| URL | 查看原文 |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/39024 |
| Collection | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | Z. Q. Hu,Y. Zhang,Y. L. Liu,et al. CORROSION BEHAVIOR OF 8090 AL-LI ALLOY[J]. Corrosion,1993,49(6):491-498. |
| APA | Z. Q. Hu,Y. Zhang,Y. L. Liu,&Z. Y. Zhu.(1993).CORROSION BEHAVIOR OF 8090 AL-LI ALLOY.Corrosion,49(6),491-498. |
| MLA | Z. Q. Hu,et al."CORROSION BEHAVIOR OF 8090 AL-LI ALLOY".Corrosion 49.6(1993):491-498. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment