INFLUENCE OF LOADING FREQUENCY ON TRANSIENT CURRENT BEHAVIOR OF FE-26CR-1MO DURING LOW-CYCLE CORROSION-FATIGUE IN 1M H2SO4 AND 0.6M NACL SOLUTIONS

IMR OpenIR

	INFLUENCE OF LOADING FREQUENCY ON TRANSIENT CURRENT BEHAVIOR OF FE-26CR-1MO DURING LOW-CYCLE CORROSION-FATIGUE IN 1M H2SO4 AND 0.6M NACL SOLUTIONS
	J. Q. Wang; J. Li; Z. F. Wang; Z. Y. Zhu; W. Ke; Z. G. Wang; Q. S. Zang
	1993
发表期刊	Scripta Metallurgica Et Materialia
ISSN	0956-716X
卷号	29 期号:11 页码:1415-1420
部门归属	inst met sci & technol,state key lab fatigue & fracture mat,shenyang 110015,peoples r china.;wang, jq (reprint author), acad sinica,inst corrs & protect met,corros sci lab,shenyang 110015,peoples r china
关键词	Stainless-steel Strain
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/39128
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	J. Q. Wang,J. Li,Z. F. Wang,et al. INFLUENCE OF LOADING FREQUENCY ON TRANSIENT CURRENT BEHAVIOR OF FE-26CR-1MO DURING LOW-CYCLE CORROSION-FATIGUE IN 1M H2SO4 AND 0.6M NACL SOLUTIONS[J]. Scripta Metallurgica Et Materialia,1993,29(11):1415-1420.
APA	J. Q. Wang.,J. Li.,Z. F. Wang.,Z. Y. Zhu.,W. Ke.,...&Q. S. Zang.(1993).INFLUENCE OF LOADING FREQUENCY ON TRANSIENT CURRENT BEHAVIOR OF FE-26CR-1MO DURING LOW-CYCLE CORROSION-FATIGUE IN 1M H2SO4 AND 0.6M NACL SOLUTIONS.Scripta Metallurgica Et Materialia,29(11),1415-1420.
MLA	J. Q. Wang,et al."INFLUENCE OF LOADING FREQUENCY ON TRANSIENT CURRENT BEHAVIOR OF FE-26CR-1MO DURING LOW-CYCLE CORROSION-FATIGUE IN 1M H2SO4 AND 0.6M NACL SOLUTIONS".Scripta Metallurgica Et Materialia 29.11(1993):1415-1420.