A STUDY ON FRACTAL DIMENSION OF FRACTURE SURFACE CREATED BY STRESS-CORROSION CRACKING IN HIGH-STRENGTH STEELS

IMR OpenIR

	A STUDY ON FRACTAL DIMENSION OF FRACTURE SURFACE CREATED BY STRESS-CORROSION CRACKING IN HIGH-STRENGTH STEELS
	Q. Y. Long; J. Chen; J. Z. Chen; Z. Q. Mu; C. W. Lung
	1992
发表期刊	Scripta Metallurgica Et Materialia
ISSN	0956-716X
卷号	27 期号:10 页码:1319-1324
部门归属	acad sinica,inst met res,fatigue & fracture mat lab,shenyang 110015,peoples r china.;long, qy (reprint author), acad sinica,int ctr mat phys,72 wenhua rd,shenyang 110015,peoples r china
关键词	Character
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/39265
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Q. Y. Long,J. Chen,J. Z. Chen,et al. A STUDY ON FRACTAL DIMENSION OF FRACTURE SURFACE CREATED BY STRESS-CORROSION CRACKING IN HIGH-STRENGTH STEELS[J]. Scripta Metallurgica Et Materialia,1992,27(10):1319-1324.
APA	Q. Y. Long,J. Chen,J. Z. Chen,Z. Q. Mu,&C. W. Lung.(1992).A STUDY ON FRACTAL DIMENSION OF FRACTURE SURFACE CREATED BY STRESS-CORROSION CRACKING IN HIGH-STRENGTH STEELS.Scripta Metallurgica Et Materialia,27(10),1319-1324.
MLA	Q. Y. Long,et al."A STUDY ON FRACTAL DIMENSION OF FRACTURE SURFACE CREATED BY STRESS-CORROSION CRACKING IN HIGH-STRENGTH STEELS".Scripta Metallurgica Et Materialia 27.10(1992):1319-1324.