| Failure behavior of nano-SiO2 fillers epoxy coating under hydrostatic pressure | |
| L. Liu; Y. Cui; Y. Li; T. Zhang; F. H. Wang | |
| 2012 | |
| Source Publication | Electrochimica Acta
 |
| ISSN | 0013-4686 |
| Volume | 62Pages:42-50 |
| Abstract | The failure of organic coating (epoxy resin filled with 5 mass% nano-SiO2 particles) on mild steel under high hydrostatic pressure (35 atm) has been studied compared with that under atmospheric pressure (1 atm), using impedance measurements, gravimetric testing, adhesion testing and scanning electron microscopy (SEM). The results show that high hydrostatic pressure accelerated the failure of the organic coating by promoting diffusion of water in the coating, which speeds up water spread and electrochemical reactions at the interface. The roughness of the coating and steel has been discussed from point of view of their respective fractal dimensions Pic and Dfx, as deduced from impedance measurements (C) 2011 Elsevier Ltd. All rights reserved. |
| description.department | [liu, li; cui, yu; li, ying; wang, fuhui] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. [cui, yu; zhang, tao; wang, fuhui] harbin engn univ, minist educ, key lab superlight mat & surface technol, corros & protect lab, harbin 150001, peoples r china.;li, y (reprint author), chinese acad sci, inst met res, state key lab corros & protect, wencui rd 62, shenyang 110016, peoples r china.;liying@imr.ac.cn |
| Keyword | High Hydrostatic Pressure Deep Ocean Organic Coating Fractal Dimension Electrochemical Impedance Spectroscopy Organic Coatings Capacitance Measurements Water Transport Coated Metals Degradation Models Steel |
| URL | 查看原文 |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/60115 |
| Collection | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | L. Liu,Y. Cui,Y. Li,et al. Failure behavior of nano-SiO2 fillers epoxy coating under hydrostatic pressure[J]. Electrochimica Acta,2012,62:42-50. |
| APA | L. Liu,Y. Cui,Y. Li,T. Zhang,&F. H. Wang.(2012).Failure behavior of nano-SiO2 fillers epoxy coating under hydrostatic pressure.Electrochimica Acta,62,42-50. |
| MLA | L. Liu,et al."Failure behavior of nano-SiO2 fillers epoxy coating under hydrostatic pressure".Electrochimica Acta 62(2012):42-50. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment