Strength and ductility of 316L austenitic stainless steel strengthened by nano-scale twin bundles

IMR OpenIR

	Strength and ductility of 316L austenitic stainless steel strengthened by nano-scale twin bundles
	F. K. Yan; G. Z. Liu; N. R. Tao; K. Lu
	2012
发表期刊	Acta Materialia
ISSN	1359-6454
卷号	60 期号:3 页码:1059-1071
摘要	By means of dynamic plastic deformation (DPD) with high strain rates, a bulk nanostructured 316L austenitic stainless steel consisting of nano-sized grains embedded with bundles of nanometer-thick deformation twins was synthesized. The average transverse grain size is similar to 33 nm and the twin/matrix lamellar thickness is similar to 20 nm. The nano-twin bundles constitute similar to 24% in volume. The nanostructured samples exhibit a high tensile strength of similar to 1400 MPa but a limited ductility with a uniform elongation of similar to 2%. Subsequent thermal annealing of the as-DPD samples in a temperature range of 730-800 degrees C led to a single-phased austenite structure consisting of static recrystallized (SRX) micro-sized grains embedded with remaining nano-twin bundles and nano-grains. The annealed DPD samples exhibit an enhanced strength-ductility synergy and much more enhanced work-hardening rates than the as-deformed samples. Work-hardening rates of the annealed DPD samples can be even higher than that of the original CG sample. Tensile ductility was found to increase almost linearly with the volume fraction of SRX grains. A combination of 1.0 GPa tensile strength with an elongation-to-failure of similar to 27% is achieved in the annealed DPD 316L stainless steel samples. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
部门归属	[yan, f. k.; liu, g. z.; tao, n. r.; lu, k.] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china.;lu, k (reprint author), chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china.;lu@imr.ac.cn
关键词	Nanostructures Nano-twin Strengthening 316l Stainless Steel Dynamic Plastic Deformation Strength Ductility Synergy Dynamic Plastic-deformation Centered-cubic Metals Strain-rate Microstructural Evolution Mechanical-properties Induced Transformation Tensile Properties Induced Martensite Copper Nucleation
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/60383
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	F. K. Yan,G. Z. Liu,N. R. Tao,et al. Strength and ductility of 316L austenitic stainless steel strengthened by nano-scale twin bundles[J]. Acta Materialia,2012,60(3):1059-1071.
APA	F. K. Yan,G. Z. Liu,N. R. Tao,&K. Lu.(2012).Strength and ductility of 316L austenitic stainless steel strengthened by nano-scale twin bundles.Acta Materialia,60(3),1059-1071.
MLA	F. K. Yan,et al."Strength and ductility of 316L austenitic stainless steel strengthened by nano-scale twin bundles".Acta Materialia 60.3(2012):1059-1071.