	Influences of reflow time and strain rate on interfacial fracture behaviors of Sn-4Ag/Cu solder joints
	Q. K. Zhang; Z. F. Zhang
	2012
发表期刊	Journal of Applied Physics
ISSN	0021-8979
卷号	112 期号:6
摘要	In this study, the influences of reflow time and strain rate on interfacial fracture behaviors of the Sn-4Ag/Cu solder joints were investigated through in-situ observation. The interfacial microstructures of the solder joints reflowed for different times were first observed by scanning electronic microscope and measuring laser confocal microscope. Then tensile tests of the solder joints were conducted using in-situ tensile stage at different strain rates, and the interfacial fracture processes were in-situ observed. The observation results reveal that the thickness and surface roughness of the interfacial Cu6Sn5 layers increase linearly with increasing square root of the reflow time. Due to the serious strain concentration, fractures of the solder joints occur around the solder/Cu6Sn5 interface. The solder joints reflowed for a short time usually fracture inside the solder close to the joint interface, while the long-time reflowed solder joints are more apt to fracture in the interfacial Cu6Sn5 layer, because the stress applied on the Cu6Sn5 grains increases with increasing reflow time and grain size of Cu6Sn5. The solder joints reflowed for moderate time have the highest fracture resistance. At higher strain rate, the solder can apply a higher stress on Cu6Sn5 layer prior to its fracture, making the latter more apt to fracture. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4754016]
部门归属	[zhang, q. k.; zhang, z. f.] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china. [zhang, q. k.] zhengzhou res inst mech engn, state key lab adv brazing filler met & technol, zhengzhou 450001, peoples r china.;zhang, zf (reprint author), chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china.;zhfzhang@imr.ac.cn
关键词	Lead-free Solders To-brittle Transition Intermetallic Compounds Deformation-behavior Tensile Properties Shear-strength Sn Sn-3.5ag Tin Cu
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/60454
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Q. K. Zhang,Z. F. Zhang. Influences of reflow time and strain rate on interfacial fracture behaviors of Sn-4Ag/Cu solder joints[J]. Journal of Applied Physics,2012,112(6).
APA	Q. K. Zhang,&Z. F. Zhang.(2012).Influences of reflow time and strain rate on interfacial fracture behaviors of Sn-4Ag/Cu solder joints.Journal of Applied Physics,112(6).
MLA	Q. K. Zhang,et al."Influences of reflow time and strain rate on interfacial fracture behaviors of Sn-4Ag/Cu solder joints".Journal of Applied Physics 112.6(2012).