Studies of impedance models and water transport behaviours of epoxy coating at hydrostatic pressure of seawater
J. Liu; X. B. Li; J. Wang; T. Y. Luo; X. M. Wang
2013
Source PublicationProgress in Organic Coatings
ISSN0300-9440
Volume76Issue:7-8Pages:1075-1081
AbstractIn simulated deep-sea environment, the evolution of impedance models and water transport behaviours of epoxy coating on 907A steel surface were studied by electrochemical impedance spectroscopy (EIS). By the fitting analysis of EIS, three equivalent electrical circuits (EEC) were proposed to the epoxy coating/907A steel system at 25 atm hydrostatic pressure for different immersion stages: good barrier property of the coating (Circuit A), active corrosion period at the beginning (Circuit B), and finally emergency of diffusion impedance (Circuit C). The evolution of coating capacitance indicated that water transport followed the Fickian diffusion behaviour during the initial stage at 25 atm hydrostatic pressure and at atmospheric pressure. High pressure accelerated diffusion rates of seawater into epoxy coatings, this shortened the period of water uptake of the coating that reached saturation. The similar chemical structures of epoxy coatings at two kinds of hydrostatic pressure were found from the Fourier transform infrared spectroscopy (Fr-IR) - attenuated total reflection (ATR) measurements. High pressure of seawater accelerated the coating physical failure, and chemical structures of the coating did not change during the experiment. (C) 2013 Elsevier B.V. All rights reserved.
description.department[liu jie ; luo tian-yuan] southwest technol & engn res inst, chongqing 400039, peoples r china. [liu jie ; wang xiao-ming] nanjing univ sci & technol, sch mech engn, nanjing 210094, jiangsu, peoples r china. [li xiang-bo] state key lab marine corros & protect, qingdao 266071, peoples r china. [wang jia] state key lab corros & protect, shenyang 110016, peoples r china. ; liu, j (reprint author), southwest technol & engn res inst, chongqing 400039, peoples r china. ; liujie6573@163.com
KeywordEpoxy Coating Impedance Models Water Transport Hydrostatic Pressure Of Seawater Nacl Solution Corrosion Protection Organic Coatings Aluminum-alloys Coated Metals Paint Systems Eis Spectroscopy Diffusion Films
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/71368
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
J. Liu,X. B. Li,J. Wang,et al. Studies of impedance models and water transport behaviours of epoxy coating at hydrostatic pressure of seawater[J]. Progress in Organic Coatings,2013,76(7-8):1075-1081.
APA J. Liu,X. B. Li,J. Wang,T. Y. Luo,&X. M. Wang.(2013).Studies of impedance models and water transport behaviours of epoxy coating at hydrostatic pressure of seawater.Progress in Organic Coatings,76(7-8),1075-1081.
MLA J. Liu,et al."Studies of impedance models and water transport behaviours of epoxy coating at hydrostatic pressure of seawater".Progress in Organic Coatings 76.7-8(2013):1075-1081.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[J. Liu]'s Articles
[X. B. Li]'s Articles
[J. Wang]'s Articles
Baidu academic
Similar articles in Baidu academic
[J. Liu]'s Articles
[X. B. Li]'s Articles
[J. Wang]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[J. Liu]'s Articles
[X. B. Li]'s Articles
[J. Wang]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.