Novel phenomenon on valence unvariation of doping ion in Yb:YAG transparent ceramics using MgO additives
Z. W. Lu; T. C. Lu; N. Wei; B. Y. Ma; W. Zhang; F. Li; Y. B. Guan
2013
Source PublicationJournal of Wuhan University of Technology-Materials Science Edition
ISSN1000-2413
Volume28Issue:2Pages:320-324
AbstractYb:YAG nanopowders were synthesized by the alcohol-water co-precipitation method adding MgO as sintering additives. Appropriate amount of MgO adding can restrict the agglomeration and reduce the particle size of Yb:YAG powders. When the MgO content was 0.04wt%, well-dispersed Yb:YAG powders with ellipsoidal particles of less than 100 nm diameter were obtained. The experimental results showed the valence variation of doping ion Yb3+ would not appear when adding MgO as sintering additives, so ceramics showed colorless transparent instead of green due to Yb2+ color center using traditional SiO2 as additives. The transmission of the sintered Yb:YAG ceramics can reach 80.6% even without annealing. Ceramic morphology showed that the grains had uniform-distribution with the size of 10 mu m or so, and no impurity and pore existed in the grain boundary and crystalline while using optimal sintering conditions.
description.department[lu zhongwen ; lu tiecheng ; wei nian ; ma benyuan ; zhang wei ; li feng ; guan yongbing] sichuan univ, dept phys, minist educ, key lab radiat phys & technol, chengdu 610064, peoples r china. [lu tiecheng] chinese acad sci, int ctr mat phys, shenyang 110015, peoples r china. ; lu, tc (reprint author), sichuan univ, dept phys, minist educ, key lab radiat phys & technol, chengdu 610064, peoples r china. ; luwei3024@163.com ; lutiecheng@scu.edu.cn
KeywordYb:Yag Mgo Transparent Ceramics Sintering Additives Valence Unvariation Mgal2o4 Spinel Yb-yag Laser Fabrication
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/71394
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Z. W. Lu,T. C. Lu,N. Wei,et al. Novel phenomenon on valence unvariation of doping ion in Yb:YAG transparent ceramics using MgO additives[J]. Journal of Wuhan University of Technology-Materials Science Edition,2013,28(2):320-324.
APA Z. W. Lu.,T. C. Lu.,N. Wei.,B. Y. Ma.,W. Zhang.,...&Y. B. Guan.(2013).Novel phenomenon on valence unvariation of doping ion in Yb:YAG transparent ceramics using MgO additives.Journal of Wuhan University of Technology-Materials Science Edition,28(2),320-324.
MLA Z. W. Lu,et al."Novel phenomenon on valence unvariation of doping ion in Yb:YAG transparent ceramics using MgO additives".Journal of Wuhan University of Technology-Materials Science Edition 28.2(2013):320-324.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Z. W. Lu]'s Articles
[T. C. Lu]'s Articles
[N. Wei]'s Articles
Baidu academic
Similar articles in Baidu academic
[Z. W. Lu]'s Articles
[T. C. Lu]'s Articles
[N. Wei]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Z. W. Lu]'s Articles
[T. C. Lu]'s Articles
[N. Wei]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.