Effects of filler metal composition on the microstructure and mechanical properties for ER NiCrFe-7 multi-pass weldments

IMR OpenIR

	Effects of filler metal composition on the microstructure and mechanical properties for ER NiCrFe-7 multi-pass weldments
	W. L. Mo; S. P. Lu; D. Z. Li; Y. Y. Li
	2013
发表期刊	Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
ISSN	0921-5093
卷号	582 页码:326-337
摘要	The effects of the minor elements Ti and Nb on the microstructure and mechanical properties for multipass weldments from the alloy ER NiCrFe-7 were studied using an optical microscope (OM), scanning electron microscope (SEM), transmission electron microscope (TEM), electron probe micro analysis (EPMA), as well as tensile and bend tests. The results show that grain size does not change significantly by increasing the Ti content from 0.28 wt% to 0.87 wt% in the weld metal (WM), whereas the grain boundaries become tortuous. The intragranular precipitate in the WM with Ti are AlO and Ti(C, N), whereas the intragranular precipitate in the WM with Nb are AlO and MX (M=Nb, Ti, X= C, N). As the Ti and Nb content increased in the WM, more MX was produced. Furthermore, the majority of C was fixed in the grain, not segregated to the grain boundaries; and less M23C6 (M=Cr, Fe) formed at the grain boundaries. Fewer ductility-dip-cracking (DDC) was observed for WM with higher levels of Ti and Nb. The tensile strength and elongation simultaneously increased with an increase in Ti and Nb in WM. The number and length of the cracks in the bend specimens decreased upon adding Ti and Nb. (C) 2013 Elsevier B.V. All rights reserved.
部门归属	[mo, wenlin ; lu, shanping ; li, dianzhong ; li, yiyi] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; lu, sp (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, 72 wenhua rd, shenyang 110016, peoples r china. ; shplu@imr.ac.cn
关键词	Er Nicrfe-7 Ti Nb Multi-pass Weldments Microstructure Mechanical Properties Ductility-dip Cracking Reheated Weld Metal Stress-corrosion Cracking High-temperature Behavior Grain-boundary Character Heat-affected-zone Ni-based Alloys Cr-fe Alloys Part Ii Microcracking Susceptibility
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/71411
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	W. L. Mo,S. P. Lu,D. Z. Li,et al. Effects of filler metal composition on the microstructure and mechanical properties for ER NiCrFe-7 multi-pass weldments[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2013,582:326-337.
APA	W. L. Mo,S. P. Lu,D. Z. Li,&Y. Y. Li.(2013).Effects of filler metal composition on the microstructure and mechanical properties for ER NiCrFe-7 multi-pass weldments.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,582,326-337.
MLA	W. L. Mo,et al."Effects of filler metal composition on the microstructure and mechanical properties for ER NiCrFe-7 multi-pass weldments".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 582(2013):326-337.