| Effects of Filler Metal Composition on Inclusions and Inclusion Defects for ER NiCrFe-7 Weldments | |
| W. L. Mo; S. P. Lu; D. Z. Li; Y. Y. Li | |
| 2013 | |
| Source Publication | Journal of Materials Science & Technology
 |
| ISSN | 1005-0302 |
| Volume | 29Issue:5Pages:458-466 |
| Abstract | The effects of filler metal (FM) composition on inclusions and inclusion defects for ER NiCrFe-7 weldments have been investigated and analyzed. Results show that as Al, Ti content in FM increases from 0.14 wt% Al, 0.30 wt% Ti to 0.42 wt% Al, 0.92 wt% Ti, the Al, Ti reduction will increase during welding. Inclusion defects (point-like defects named by welding workers) are prone to form in the high Al, Ti content weldments. Inclusion defects with Mg, Ca, Al, and Ti as major metallic elements have been found on the surface and interior of the weldments, as Al, Ti content in FM is over 0.29 wt% Al, 0.62 wt% Ti. Less Ti content in FM cannot prevent ductility-dip-cracking (DDC) through producing enough intragranular precipitates and lessening intergranular M23C6 precipitates. Nb can be used to replace Ti to reduce the sensitivity of the DDC in the NiCrFe-7 alloy weldments. |
| description.department | [mo, wenlin ; lu, shanping ; li, dianzhong ; li, yiyi] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; lu, sp (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; shplu@imr.ac.cn |
| Keyword | Filler Metal Composition Er Nicrfe-7 Inclusions Inclusion Defects Ductility-dip-cracking Ductility-dip Cracking Multipass Weld Metal High-temperature Behavior Grain-boundary Character Ni-based Alloys Heat-treatment Part Ii Microcracking Susceptibility Intergranular Corrosion Mechanical-properties |
| URL | 查看原文 |
| Language | 英语 |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/71412 |
| Collection | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | W. L. Mo,S. P. Lu,D. Z. Li,et al. Effects of Filler Metal Composition on Inclusions and Inclusion Defects for ER NiCrFe-7 Weldments[J]. Journal of Materials Science & Technology,2013,29(5):458-466. |
| APA | W. L. Mo,S. P. Lu,D. Z. Li,&Y. Y. Li.(2013).Effects of Filler Metal Composition on Inclusions and Inclusion Defects for ER NiCrFe-7 Weldments.Journal of Materials Science & Technology,29(5),458-466. |
| MLA | W. L. Mo,et al."Effects of Filler Metal Composition on Inclusions and Inclusion Defects for ER NiCrFe-7 Weldments".Journal of Materials Science & Technology 29.5(2013):458-466. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment