|Influence of microstructural evolution on tensile properties of friction stir welded joint of rolled SiCp/AA2009-T351 sheet|
|D. R. Ni; D. L. Chen; D. Wang; B. L. Xiao; Z. Y. Ma
|Source Publication||Materials & Design
|Abstract||To elucidate the intrinsic factors which decreased the strength and ductility of friction stir welded (FSW) joints of precipitation-strengthened aluminium matrix composites, 3 mm thick rolled 17 vol.% SiCp/AA2009 composite sheet in T351 condition was subjected to FSW and detailed microstructure examinations. The microstructure of the base metal was characterized by high dislocation density and few precipitates. After FSW, low dislocation density and a few coarse theta (Al2Cu) precipitates were detected in the nugget zone, whereas a great number of coarse theta and S (Al2CuMg) precipitates and greatly decreased dislocation density were observed in the heat-affected zone (HAZ). Therefore, the HAZ showed the lowest hardness throughout the whole joint and became the weakest region, where fracture occurred during tensile testing. The FSW joint exhibited a good combination of strength and ductility with the ultimate tensile strength, elongation and joint efficiency reaching 443 MPa, 4.7% and 77%, respectively. (c) 2013 Elsevier Ltd. All rights reserved.|
|description.department||[ni, d. r.
; wang, d.
; xiao, b. l.
; ma, z. y.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. [chen, d. l.] ryerson univ, dept mech & ind engn, toronto, on m5b 2k3, canada.
; ma, zy (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, 72 wenhua rd, shenyang 110016, peoples r china.
|Keyword||Friction Stir Welding
Differential Scanning Calorimetry
D. R. Ni,D. L. Chen,D. Wang,et al. Influence of microstructural evolution on tensile properties of friction stir welded joint of rolled SiCp/AA2009-T351 sheet[J]. Materials & Design,2013,51:199-205.
D. R. Ni,D. L. Chen,D. Wang,B. L. Xiao,&Z. Y. Ma.(2013).Influence of microstructural evolution on tensile properties of friction stir welded joint of rolled SiCp/AA2009-T351 sheet.Materials & Design,51,199-205.
D. R. Ni,et al."Influence of microstructural evolution on tensile properties of friction stir welded joint of rolled SiCp/AA2009-T351 sheet".Materials & Design 51(2013):199-205.
|Files in This Item:||
||There are no files associated with this item.
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.