Effect of Hydrostatic Pressure on the Corrosion Behavior of a Low Alloy Steel
H. J. Sun; L. Liu; Y. Li; F. H. Wang
2013
Source PublicationJournal of the Electrochemical Society
ISSN0013-4651
Volume160Issue:3Pages:C89-C96
AbstractThe effect of hydrostatic pressure (HP) on the corrosion behavior of low alloy steel in 3.5% NaCl was studied in a pressure vessel using gravimetric, electrochemical and imaging techniques. The results indicate that HP influences the corrosion behavior of steel to different extents all through the immersion period: in the initial immersion (first 5 days), the corrosion rate at 35 atm is obviously higher than that at 1 atm; which is followed by a period of no obvious difference between the two pressures; and after 15 days, the corrosion rate at 35 atm is only slightly higher than that at 1 atm. Generally, it stimulates the corrosion process, especially during the initial immersion. Further study reveals that the increased corrosion rate at high HP during the initial immersion could be related to the enhanced Cl- adsorption. After, the formation of integrated rust layer, HP affects the chemical and physical properties of rust layer. Consequently, it is more conducive for the transport of Cl- at high HP, which further gives rise to the accelerated corrosion. This study aims to be conducive to the fundamental understanding of the corrosion behavior of steel in deep ocean environments. (C) 2013 The Electrochemical Society. [DOI: 10.1149/2.040303jes] All rights reserved.
description.department[sun, haijing ; liu, li ; li, ying ; wang, fuhui] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; sun, hj (reprint author), chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; liliu@imr.ac.cn ; liying@imr.ac.cn
KeywordSlightly Alkaline-solutions Sea-water Protective Ability Passive Film Carbon Steel Mild-steel Layer Iron Environments Temperature
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/71477
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
H. J. Sun,L. Liu,Y. Li,et al. Effect of Hydrostatic Pressure on the Corrosion Behavior of a Low Alloy Steel[J]. Journal of the Electrochemical Society,2013,160(3):C89-C96.
APA H. J. Sun,L. Liu,Y. Li,&F. H. Wang.(2013).Effect of Hydrostatic Pressure on the Corrosion Behavior of a Low Alloy Steel.Journal of the Electrochemical Society,160(3),C89-C96.
MLA H. J. Sun,et al."Effect of Hydrostatic Pressure on the Corrosion Behavior of a Low Alloy Steel".Journal of the Electrochemical Society 160.3(2013):C89-C96.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[H. J. Sun]'s Articles
[L. Liu]'s Articles
[Y. Li]'s Articles
Baidu academic
Similar articles in Baidu academic
[H. J. Sun]'s Articles
[L. Liu]'s Articles
[Y. Li]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[H. J. Sun]'s Articles
[L. Liu]'s Articles
[Y. Li]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.