Dynamic Recrystallization Mechanism of Inconel 690 Superalloy During Hot deformation at High Strain Rate | |
B. Wang; S. H. Zhang; M. Cheng; H. W. Song | |
2013 | |
Source Publication | Journal of Materials Engineering and Performance
![]() |
ISSN | 1059-9495 |
Volume | 22Issue:8Pages:2382-2388 |
Abstract | The hot deformation characteristics of Inconel 690 superalloy were investigated on the Gleeble-3800 thermal-mechanical simulator. The testing temperatures were in the range of 1000-1200 A degrees C, the strain rate was 10 s(-1), and the maximum true strain was 0.9. Optical microscopy, transmission electron microscopy, and electron backscatter diffraction techniques were employed to analyze the microstructure evolution and nucleation mechanisms of dynamic recrystallization (DRX). The results show that multiple-cycle discontinuous dynamic recrystallization (DDRX) occurs in the process of hot deformation under the conditions above. DRX grain size decreases with decreasing temperature and increasing strain. DDRX with sub-grains directly transforming into grains is the dominating nucleation mechanism of DRX. And, the nucleation mechanism of bulging of the original grain boundaries can only be considered as an assistant nucleation mechanism of DRX, which mainly occurs in the beginning of the deformation. |
description.department | [wang, bin ; zhang, shi-hong ; cheng, ming ; song, hong-wu] chinese acad sci, inst met res, shenyang 110016, peoples r china. ; wang, b (reprint author), chinese acad sci, inst met res, shenyang 110016, peoples r china. ; shzhang@imr.ac.cn |
Keyword | Drx Hot Deformation Inconel 690 Superalloy Microstructure Evolution Alloy Behavior Microstructure Evolution Aluminum Growth Tubes |
URL | 查看原文 |
Language | 英语 |
Document Type | 期刊论文 |
Identifier | http://ir.imr.ac.cn/handle/321006/71511 |
Collection | 中国科学院金属研究所 |
Recommended Citation GB/T 7714 | B. Wang,S. H. Zhang,M. Cheng,et al. Dynamic Recrystallization Mechanism of Inconel 690 Superalloy During Hot deformation at High Strain Rate[J]. Journal of Materials Engineering and Performance,2013,22(8):2382-2388. |
APA | B. Wang,S. H. Zhang,M. Cheng,&H. W. Song.(2013).Dynamic Recrystallization Mechanism of Inconel 690 Superalloy During Hot deformation at High Strain Rate.Journal of Materials Engineering and Performance,22(8),2382-2388. |
MLA | B. Wang,et al."Dynamic Recrystallization Mechanism of Inconel 690 Superalloy During Hot deformation at High Strain Rate".Journal of Materials Engineering and Performance 22.8(2013):2382-2388. |
Files in This Item: | There are no files associated with this item. |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment