IMR OpenIR
Microstructure and mechanical properties of Mg-Zn-Y-Nd-Zr alloys
J. Wang; R. D. Liu; X. G. Dong; Y. S. Yang
2013
Source PublicationJournal of Rare Earths
ISSN1002-0721
Volume31Issue:6Pages:616-621
AbstractThe microstructure and tensile properties of the as-cast and solution treatment Mg-4.5Zn-1Y-xNd-0.5Zr (x=0, 1 wt.%, 2 wt.%, 3 wt.%) alloys were investigated. The results showed that the microstructure of Mg-4.5Zn-1Y-0.5Zr alloy consisted of alpha-Mg, Zn-Zr, W (Mg3Y2Zn3) and I (Mg3YZn6) phases. With the addition of Nd, I-phase disappeared and Mg3Y2Zn3 phase changed into Mg-3(Nd, Y)(2)Zn-3 phase. When the content of Nd reached 3 wt.%, T phase, i.e., ternary Mg-Zn-Nd phase, formed. In addition, with the increase of Nd content in the alloys, the secondary dendritic arm spacing decreased, while the amount of intermetallic phases increased. For as-cast Mg-4.5Zn-1Y-xNd-0.5Zr alloys, after solution treatment, microsegregation was eliminated and the shape of eutectic structure of alpha-Mg+W transformed from lamellar into spherical. The tensile strength and elongation of Mg-4.5Zn-1Y-3Nd-0.5Zr alloy were increased from 219.2 MPa and 11.0% to 247.5 MPa and 20.0%, respectively.
description.department[wang jing ; liu ruidong ; dong xuguang ; yang yuansheng] chinese acad sci, inst met res, shenyang 110016, peoples r china. [yang yuansheng] shandong acad sci, new mat res inst, jinan 250014, peoples r china. ; yang, ys (reprint author), chinese acad sci, inst met res, shenyang 110016, peoples r china. ; ysyang@imr.ac.cn
KeywordMg-zn-y-nd-zr Alloys Homogenizing Treatment Microstructure Mechanical Properties Rare Earths Automotive Industry Magnesium Alloy As-cast Behavior Tensile X=0
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/71530
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
J. Wang,R. D. Liu,X. G. Dong,et al. Microstructure and mechanical properties of Mg-Zn-Y-Nd-Zr alloys[J]. Journal of Rare Earths,2013,31(6):616-621.
APA J. Wang,R. D. Liu,X. G. Dong,&Y. S. Yang.(2013).Microstructure and mechanical properties of Mg-Zn-Y-Nd-Zr alloys.Journal of Rare Earths,31(6),616-621.
MLA J. Wang,et al."Microstructure and mechanical properties of Mg-Zn-Y-Nd-Zr alloys".Journal of Rare Earths 31.6(2013):616-621.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[J. Wang]'s Articles
[R. D. Liu]'s Articles
[X. G. Dong]'s Articles
Baidu academic
Similar articles in Baidu academic
[J. Wang]'s Articles
[R. D. Liu]'s Articles
[X. G. Dong]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[J. Wang]'s Articles
[R. D. Liu]'s Articles
[X. G. Dong]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.