Effect of carbon content on the recrystallization of a single crystal nickel-based superalloy
L. Wang; G. Xie; L. H. Lou
2013
发表期刊Materials Letters
ISSN0167-577X
卷号109页码:154-157
摘要Carbon has recently been reintroduced to single crystal (SX) superalloys because of its beneficial effects, such as reducing the occurrence of casting defects and enhancing the tolerance of low angle grain boundaries. Meanwhile, the addition of carbon leads to changes in the carbide morphology and volume fraction and may subsequently affect the recrystallization (RX) behavior. The purpose of this paper was to identify the effect of the carbon content on RX in an SX nickel-based superalloy. The SX specimens were prepared with an identical crystal orientation but different carbon contents. It was found that with the increase of the carbon content from 0.012 wt% to 0.17 wt%, the volume fraction of carbides increased linearly, while the average size of the carbides was nearly unchanged. After shot peening and heat treatment, a layer of RX grains was generated on the surface. As the carbon content was increased, the RX depth increased at first and later decreased. These changes were interpreted as the combined effect of the carbides on the stored energy during deformation and the pinning force during RX grain growth. (C) 2013 Elsevier B.V. All rights reserved.
部门归属[wang, l. ; xie, g. ; lou, l. h.] chinese acad sci, inst met res, superalloys div, shenyang 110016, peoples r china. ; wang, l (reprint author), chinese acad sci, inst met res, superalloys div, shenyang 110016, peoples r china. ; wangli@imr.ac.cn
关键词Recrystallization Particles Carbon Single Crystal Superalloy Carbides
URL查看原文
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/71540
专题中国科学院金属研究所
推荐引用方式
GB/T 7714
L. Wang,G. Xie,L. H. Lou. Effect of carbon content on the recrystallization of a single crystal nickel-based superalloy[J]. Materials Letters,2013,109:154-157.
APA L. Wang,G. Xie,&L. H. Lou.(2013).Effect of carbon content on the recrystallization of a single crystal nickel-based superalloy.Materials Letters,109,154-157.
MLA L. Wang,et al."Effect of carbon content on the recrystallization of a single crystal nickel-based superalloy".Materials Letters 109(2013):154-157.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[L. Wang]的文章
[G. Xie]的文章
[L. H. Lou]的文章
百度学术
百度学术中相似的文章
[L. Wang]的文章
[G. Xie]的文章
[L. H. Lou]的文章
必应学术
必应学术中相似的文章
[L. Wang]的文章
[G. Xie]的文章
[L. H. Lou]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。