IMR OpenIR
Anisotropic friction behaviour of highly oriented pyrolytic graphite
J. K. Xiao; L. Zhang; K. C. Zhou; J. G. Li; X. L. Xie; Z. Y. Li
2013
Source PublicationCarbon
ISSN0008-6223
Volume65Pages:53-62
AbstractFriction tests on two surfaces of highly oriented pyrolytic graphite that are parallel and perpendicular to the direction of the graphite basal plane were performed under various test conditions. The average friction coefficient value of the perpendicular surface (0.25) is higher than that of the parallel surface (0.1). The friction coefficient of both parallel and perpendicular surfaces decline when the environment is changed from wet air to wet nitrogen and the trend is more pronounced for the perpendicular surface. The perpendicular worn surface has been observed to be much rougher and owns more edge faces than the parallel worn surface. The amount of dangling bonds and chemisorbed oxygen measured on both surfaces after friction is quite different. The influence of atmosphere on the friction of graphite is attributed to the chemical reaction of dangling bonds with gases, which can affect the adhesive force of the two contact surfaces. The amount of dangling bonds generated on the sliding surface is confirmed to impact the sensitivity of graphite to gases during friction. (C) 2013 Elsevier Ltd. All rights reserved.
description.department[xiao, jinkun ; zhang, lei ; zhou, kechao ; xie, xinlin ; li, zhiyou] cent s univ, state key lab powder met, changsha 410083, peoples r china. [li, jianguo] chinese acad sci, inst met res, shenyang 110016, peoples r china. ; zhang, l (reprint author), cent s univ, state key lab powder met, changsha 410083, peoples r china. ; csuzhanglei@gmail.com
KeywordRaman-spectroscopy Diamond Surfaces Carbon Materials Wear Debris Composites Graphene Transition Disorder Braking Films
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/71593
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
J. K. Xiao,L. Zhang,K. C. Zhou,et al. Anisotropic friction behaviour of highly oriented pyrolytic graphite[J]. Carbon,2013,65:53-62.
APA J. K. Xiao,L. Zhang,K. C. Zhou,J. G. Li,X. L. Xie,&Z. Y. Li.(2013).Anisotropic friction behaviour of highly oriented pyrolytic graphite.Carbon,65,53-62.
MLA J. K. Xiao,et al."Anisotropic friction behaviour of highly oriented pyrolytic graphite".Carbon 65(2013):53-62.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[J. K. Xiao]'s Articles
[L. Zhang]'s Articles
[K. C. Zhou]'s Articles
Baidu academic
Similar articles in Baidu academic
[J. K. Xiao]'s Articles
[L. Zhang]'s Articles
[K. C. Zhou]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[J. K. Xiao]'s Articles
[L. Zhang]'s Articles
[K. C. Zhou]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.