	Thermal fatigue behaviors of Sn-4Ag/Cu solder joints at low strain amplitude
	Q. K. Zhang; Z. F. Zhang
	2013
发表期刊	Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
ISSN	0921-5093
卷号	580 页码:374-384
摘要	Thermal fatigue behaviors of the Sn-4Ag/Cu solder joints were investigated in this study. The solder joints were clamped by special designed clamps and cycled at low temperature amplitudes, their deformation morphologies were observed by Scanning Electron Microscope (SEM) and evolution in microstructures of the solder were characterized using Electron Back-scattered Diffraction (EBSD). The results reveal that the thermal fatigue process consists of a strain hardening stage and a consequent accelerating fracture stage. During the initial cycles, strain hardening of the solder keeps developing, until it becomes balance with the dynamic recovery. Due to the strain concentration, damage of the solder around the joint interface is serious and cannot release through recovery, inducing microcracks at the corner of the solder joint. After that, the nominal strength of the solder joint decreases gradually, and the damage rate accelerates with increasing cycles. The fracture surface also consists of two regions, one is covered by trace of friction and the other is similar to the shear fracture surface. Plastic deformation, grain rotation and grain coalesce occur in the solder during the thermal fatigue process, while grain subdivision or recrystallization was not observed, because the dynamic recovery keeps the strain energy of the solder at a low level. (C) 2013 Elsevier B.V. All rights reserved.
部门归属	[zhang, q. k. ; zhang, z. f.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. [zhang, q. k.] zhengzhou res inst mech engn, state key lab adv brazing filler met & technol, zhengzhou 450001, peoples r china. ; zhang, zf (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; zhfzhang@imr.ac.cn
关键词	Sn-ag/cu Solder Joints Thermal Fatigue Strain Localization Grain Rotation Dynamic Recovery Stress-relaxation Behavior Eutectic Sn-3.5ag Solder Lead-free Solders Pb-free Solders Sn-ag Tensile Properties Shear-strength Fracture-behavior Deformation Creep
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/71692
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Q. K. Zhang,Z. F. Zhang. Thermal fatigue behaviors of Sn-4Ag/Cu solder joints at low strain amplitude[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2013,580:374-384.
APA	Q. K. Zhang,&Z. F. Zhang.(2013).Thermal fatigue behaviors of Sn-4Ag/Cu solder joints at low strain amplitude.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,580,374-384.
MLA	Q. K. Zhang,et al."Thermal fatigue behaviors of Sn-4Ag/Cu solder joints at low strain amplitude".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 580(2013):374-384.