Double-peak age strengthening of cold-worked 2024 aluminum alloy
Y. L. Zhao; Z. Q. Yang; Z. Zhang; G. Y. Su; X. L. Ma
2013
Source PublicationActa Materialia
ISSN1359-6454
Volume61Issue:5Pages:1624-1638
AbstractThe microstructure and mechanical properties of a 2024 Al alloy subjected to different levels of cold-rolling at room temperature and their evolution upon ageing at 453 K were investigated by means of microhardness measurements, tensile tests and transmission electron microscopy. The cold-worked 2024 Al alloy showed double-peak age strengthening behavior. After ageing for 120 min, the samples reached the first peak strength with quite low ductility. However, simultaneous high strength and ductility were achieved by prolonged ageing of 720 mm. The first strengthening peak is due to the precipitation of fine S' precipitates. The optimized mechanical properties of high strength and suitable ductility are attributed mainly to the precipitation of Omega-phase particles at the expense of S' precipitates after ageing for 720 mm. The Omega precipitates are effective in dislocation pinning and accumulation, and they can undergo plastic deformation to some extent, leading to simultaneously improved tensile strength, work-hardening ability and ductility. The present finding sheds light on the development of processing techniques to optimize the mechanical properties of 2024 Al alloy. (C) 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
description.department[zhao, y. l. ; yang, z. q. ; ma, x. l.] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china. [zhang, z. ; su, g. y.] chinese acad sci, inst met res, precise tubing div, shenyang 110016, peoples r china. ; yang, zq (reprint author), chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china. ; yangzq34@yahoo.com
Keyword2024 Al Alloy Precipitation Omega-phase Age Strengthening Ductility High-pressure Torsion Transmission Electron-microscopy Cu-mg Alloys Omega-phase Mechanical-properties Microstructural Evolution Grain-refinement Magnesium Alloy Precipitation Al
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/71720
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Y. L. Zhao,Z. Q. Yang,Z. Zhang,et al. Double-peak age strengthening of cold-worked 2024 aluminum alloy[J]. Acta Materialia,2013,61(5):1624-1638.
APA Y. L. Zhao,Z. Q. Yang,Z. Zhang,G. Y. Su,&X. L. Ma.(2013).Double-peak age strengthening of cold-worked 2024 aluminum alloy.Acta Materialia,61(5),1624-1638.
MLA Y. L. Zhao,et al."Double-peak age strengthening of cold-worked 2024 aluminum alloy".Acta Materialia 61.5(2013):1624-1638.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Y. L. Zhao]'s Articles
[Z. Q. Yang]'s Articles
[Z. Zhang]'s Articles
Baidu academic
Similar articles in Baidu academic
[Y. L. Zhao]'s Articles
[Z. Q. Yang]'s Articles
[Z. Zhang]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Y. L. Zhao]'s Articles
[Z. Q. Yang]'s Articles
[Z. Zhang]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.