Preparation, Microstructure, and Mechanical Properties of Nb4AlC3-Nb-5(Si, Al)(3) Composites
L. Y. Zheng; J. Y. Wang; J. X. Chen; M. Y. Liu; Y. J. Sun; Y. C. Zhou
2013
Source PublicationJournal of the American Ceramic Society
ISSN0002-7820
Volume96Issue:2Pages:365-368
AbstractNiobium aluminum carbide (Nb4AlC3), as a member of the MAX phases, can retain its stiffness and strength up to over 1400 degrees C, however, the strength at room temperature is relatively low. In this work, Nb5(Si, Al)3 was used to strengthen Nb4AlC3. Nb4AlC3Nb5(Si, Al)3 composites with different amount of Nb5(Si, Al)3 were synthesized from the elemental powders by in situ hot-pressing/solidliquid reaction synthesis process. The RT flexural strength was significantly improved from 370MPa of monolithic Nb4AlC3 to 432MPa of Nb4AlC3-15vol% Nb5(Si, Al)3 composite without the degradation of its high-temperature mechanical properties. While a slightly decrease in fracture toughness occurs with the increment of Nb5(Si, Al)3 content. Meanwhile, Transmission electron microscopy (TEM) observations reveal that the interfaces between Nb4AlC3/Nb4AlC3, Nb4AlC3/Nb5(Si, Al)3, and Nb5(Si, Al)3/Nb5(Si, Al)3 are free of amorphous layers, which is also beneficial to its high-temperature mechanical properties.
description.department[zheng, l. y. ; wang, j. y. ; chen, j. x. ; liu, m. y.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. [zheng, l. y.] chinese acad sci, grad sch, beijing 100039, peoples r china. [sun, y. j. ; zhou, y. c.] arimpt, sci & technol adv funct composite lab, beijing 100076, peoples r china. ; zhou, yc (reprint author), amer ceram soc, westerville, oh 43086 usa. ; yczhou714@gmail.com
KeywordSitu Reaction Synthesis High-temperature Nb4alc3 Fabrication Phases Room
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/71724
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
L. Y. Zheng,J. Y. Wang,J. X. Chen,et al. Preparation, Microstructure, and Mechanical Properties of Nb4AlC3-Nb-5(Si, Al)(3) Composites[J]. Journal of the American Ceramic Society,2013,96(2):365-368.
APA L. Y. Zheng,J. Y. Wang,J. X. Chen,M. Y. Liu,Y. J. Sun,&Y. C. Zhou.(2013).Preparation, Microstructure, and Mechanical Properties of Nb4AlC3-Nb-5(Si, Al)(3) Composites.Journal of the American Ceramic Society,96(2),365-368.
MLA L. Y. Zheng,et al."Preparation, Microstructure, and Mechanical Properties of Nb4AlC3-Nb-5(Si, Al)(3) Composites".Journal of the American Ceramic Society 96.2(2013):365-368.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[L. Y. Zheng]'s Articles
[J. Y. Wang]'s Articles
[J. X. Chen]'s Articles
Baidu academic
Similar articles in Baidu academic
[L. Y. Zheng]'s Articles
[J. Y. Wang]'s Articles
[J. X. Chen]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[L. Y. Zheng]'s Articles
[J. Y. Wang]'s Articles
[J. X. Chen]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.