Oxidation behavior of the compound Ti-Al-Si-N/1Cr11Ni2W2MoV at 800 degrees C for 1000 h in air

IMR OpenIR

	Oxidation behavior of the compound Ti-Al-Si-N/1Cr11Ni2W2MoV at 800 degrees C for 1000 h in air
	C. J. Feng; M. S. Li; L. Xin; S. L. Zhu; Z. S. Shao; Q. Zhao; F. H. Wang
	2013
发表期刊	Surface & Coatings Technology
ISSN	0257-8972
卷号	232 页码:88-95
摘要	A Ti-A-Si-N coating was deposited on 1Cr11Ni2W2MoV stainless steel by arc ion plating(AIP) with a Ti60Al30Si10 cathode, and the prolonged oxidation behavior of the compound Ti-Al-Si-N/1Cr11Ni2W2MoV at 800 degrees C in air was investigated by TEM, SEM/EDAX, EPMA and XRD. For comparison, the oxidation of the 1Cr11Ni2W2MoV steel at 800 degrees C was also conducted. The results show that after oxidation at 800 degrees C for 1000 h, the compound Ti-Al-Si-N/1Cr11Ni2W2MoV showed excellent oxidation resistance and formed a multilayered scale. They are the top porous surface layer of TiO2, followed by a dense layer rich in Al2O3, a mixture oxides dense layer mainly composed of TiO2, SiO2 and some chromium oxide, and a bottom dense lay of chromium oxide due to the selective oxidation of the substrate. The addition of Si in the Ti-Al-N coating can promote the outwards diffusion of Al and hinder the outwards diffusion of Ti remarkably, and thus form dense and protective scale. The oxidation mechanism of the compound Ti-Al-Si-N/Cr11Ni2W2MoV at 800 degrees C for prolonged time in air was discussed. (C) 2013 Elsevier B.V. All rights reserved.
部门归属	[feng, changjie ; shao, zhisong ; zhao, qing] nanchang hangkong univ, sch mat sci & engn, nanchang 330063, peoples r china. [feng, changjie ; xin, li ; zhu, shenglong ; wang, fuhui] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. [li, mingsheng] jiangxi sci & technol normal univ, jiangxi key lab surface engn, nanchang 330013, peoples r china. ; feng, cj (reprint author), nanchang hangkong univ, sch mat sci & engn, nanchang 330063, peoples r china. ; chjfengniat@126.com
关键词	Ti-al-si-n Coating 1cr11ni2w2mov Stainless Steel Prolonged Oxidation Mechanism High-temperature Oxidation Chemical-vapor-deposition Steel Substrate Hard Coatings Thin-films Mechanical-properties Isothermal Oxidation Ti1-xalxn Coatings Thermal-stability Tialn Coatings
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/72400
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	C. J. Feng,M. S. Li,L. Xin,et al. Oxidation behavior of the compound Ti-Al-Si-N/1Cr11Ni2W2MoV at 800 degrees C for 1000 h in air[J]. Surface & Coatings Technology,2013,232:88-95.
APA	C. J. Feng.,M. S. Li.,L. Xin.,S. L. Zhu.,Z. S. Shao.,...&F. H. Wang.(2013).Oxidation behavior of the compound Ti-Al-Si-N/1Cr11Ni2W2MoV at 800 degrees C for 1000 h in air.Surface & Coatings Technology,232,88-95.
MLA	C. J. Feng,et al."Oxidation behavior of the compound Ti-Al-Si-N/1Cr11Ni2W2MoV at 800 degrees C for 1000 h in air".Surface & Coatings Technology 232(2013):88-95.