| Phase Transformation During Intercritical Tempering with High Heating Rate in a Fe-13%Cr-4%Ni-Mo Stainless Steel | |
| P. Wang; S. H. Zhang; S. P. Lu; D. Z. Li; Y. Y. Li | |
| 2013 | |
| Source Publication | Acta Metallurgica Sinica-English Letters
 |
| ISSN | 1006-7191 |
| Volume | 26Issue:6Pages:669-674 |
| Abstract | The phase transformation from martensite to austenite during intercritical tempering with high heating rate in a low carbon nnartensitic stainless steel Fe-13%Cr-4%Ni-Mo has been investigated to clarify the microstructure evolution in some regions of the weld joint heat affected zone (HAZ). The experimental results indicate that the start and finish temperatures of the martensite to austenite transformation keep constant when the heating rate is higher than. 10 K/s, and the transformation is much faster than nickel diffusion. The mechanism of the martensite to austenite transformation changes from diffusion to diffusionless during the intercritical tempering when the heating rate is higher than 10 K/s. The diffusionless transformation and higher A(s) temperature render it difficult for any austenite to remain at room temperature during the intercritical tempering with high heating rate that occurs in the HAZ. Adding a proper intercritical tempering with low heating rate can induce some reversed austenite in the rapid heated sample. |
| description.department | [wang, pei ; zhang, shenghua ; lu, shanping ; li, dianzhong ; li, yiyi] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; wang, p (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; pwang@imr.ac.cn |
| Keyword | Martensitic Stainless Steel Phase Transformation Intercritical Tempering Heating Rate Microstructure Reverse Transformation Retained Austenite Lath Martensite Mechanism Precipitation Temperature Behavior |
| URL | 查看原文 |
| Language | 英语 |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/72404 |
| Collection | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | P. Wang,S. H. Zhang,S. P. Lu,et al. Phase Transformation During Intercritical Tempering with High Heating Rate in a Fe-13%Cr-4%Ni-Mo Stainless Steel[J]. Acta Metallurgica Sinica-English Letters,2013,26(6):669-674. |
| APA | P. Wang,S. H. Zhang,S. P. Lu,D. Z. Li,&Y. Y. Li.(2013).Phase Transformation During Intercritical Tempering with High Heating Rate in a Fe-13%Cr-4%Ni-Mo Stainless Steel.Acta Metallurgica Sinica-English Letters,26(6),669-674. |
| MLA | P. Wang,et al."Phase Transformation During Intercritical Tempering with High Heating Rate in a Fe-13%Cr-4%Ni-Mo Stainless Steel".Acta Metallurgica Sinica-English Letters 26.6(2013):669-674. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment