Principles Giving High Penetration under the Double Shielded TIG Process
D. J. Li; S. P. Lu; D. Z. Li; Y. Y. Li
2014
Source PublicationJournal of Materials Science & Technology
ISSN1005-0302
Volume30Issue:2Pages:172-178
AbstractA new welding method named double shielded tungsten inert gas (TIG) has been developed to improve the TIG weld penetration. The main principles to increase the weld depth have been discussed. Results show that the critical oxygen content in the weld pool is around 100 x 10(-6) as the temperature coefficient of surface tension changes from negative to positive. The tracer test using pure silver shows that the direction of Marangoni convection changes as the oxygen content increases in the weld pool. The effect of arc constriction on the weld depth has been evaluated on a water-cooled copper plate, and the result indicates that the torch of double shielded can give a more powerful arc. Heavy oxide on the pool surface has undesirable impacts on the increasing of weld depth as the oxygen excessively accumulates in weld pool. It is possible to form chromium oxide in the weld process, while the iron oxide may form as the weld surface exposes to the air after the shielded gas moving away.
description.department[li, dongjie ; lu, shanping ; li, dianzhong ; li, yiyi] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; lu, sp (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; shplu@imr.ac.cn
KeywordMarangoni Convection Penetration Tungsten Inert Gas (Tig) Arc Oxide Gas Tungsten Arc Gta Weld Shape Oxide Fluxes Mechanism Ar-o-2 Iron
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/72484
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
D. J. Li,S. P. Lu,D. Z. Li,et al. Principles Giving High Penetration under the Double Shielded TIG Process[J]. Journal of Materials Science & Technology,2014,30(2):172-178.
APA D. J. Li,S. P. Lu,D. Z. Li,&Y. Y. Li.(2014).Principles Giving High Penetration under the Double Shielded TIG Process.Journal of Materials Science & Technology,30(2),172-178.
MLA D. J. Li,et al."Principles Giving High Penetration under the Double Shielded TIG Process".Journal of Materials Science & Technology 30.2(2014):172-178.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[D. J. Li]'s Articles
[S. P. Lu]'s Articles
[D. Z. Li]'s Articles
Baidu academic
Similar articles in Baidu academic
[D. J. Li]'s Articles
[S. P. Lu]'s Articles
[D. Z. Li]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[D. J. Li]'s Articles
[S. P. Lu]'s Articles
[D. Z. Li]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.