	Principles Giving High Penetration under the Double Shielded TIG Process
	D. J. Li; S. P. Lu; D. Z. Li; Y. Y. Li
	2014
发表期刊	Journal of Materials Science & Technology
ISSN	1005-0302
卷号	30 期号:2 页码:172-178
摘要	A new welding method named double shielded tungsten inert gas (TIG) has been developed to improve the TIG weld penetration. The main principles to increase the weld depth have been discussed. Results show that the critical oxygen content in the weld pool is around 100 x 10(-6) as the temperature coefficient of surface tension changes from negative to positive. The tracer test using pure silver shows that the direction of Marangoni convection changes as the oxygen content increases in the weld pool. The effect of arc constriction on the weld depth has been evaluated on a water-cooled copper plate, and the result indicates that the torch of double shielded can give a more powerful arc. Heavy oxide on the pool surface has undesirable impacts on the increasing of weld depth as the oxygen excessively accumulates in weld pool. It is possible to form chromium oxide in the weld process, while the iron oxide may form as the weld surface exposes to the air after the shielded gas moving away.
部门归属	[li, dongjie ; lu, shanping ; li, dianzhong ; li, yiyi] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; lu, sp (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; shplu@imr.ac.cn
关键词	Marangoni Convection Penetration Tungsten Inert Gas (Tig) Arc Oxide Gas Tungsten Arc Gta Weld Shape Oxide Fluxes Mechanism Ar-o-2 Iron
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/72484
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	D. J. Li,S. P. Lu,D. Z. Li,et al. Principles Giving High Penetration under the Double Shielded TIG Process[J]. Journal of Materials Science & Technology,2014,30(2):172-178.
APA	D. J. Li,S. P. Lu,D. Z. Li,&Y. Y. Li.(2014).Principles Giving High Penetration under the Double Shielded TIG Process.Journal of Materials Science & Technology,30(2),172-178.
MLA	D. J. Li,et al."Principles Giving High Penetration under the Double Shielded TIG Process".Journal of Materials Science & Technology 30.2(2014):172-178.