Improving the High-Temperature Oxidation Resistance of Nb4AlC3 by Silicon Pack Cementation
L. Y. Zheng; J. Y. Wang; Y. C. Zhou
2014
Source PublicationJournal of the American Ceramic Society
ISSN0002-7820
Volume97Issue:2Pages:552-561
AbstractNiobium aluminum carbide (Nb4AlC3), as a member of the MAX phases, can retain its stiffness and strength up to over 1400 degrees C. However, its applications are limited due to its poor oxidation resistance at high temperatures. In this work, silicon pack cementation has been applied to improve the oxidation resistance of Nb4AlC3. After Si pack cementation at 1200 degrees C for 6h, a dense and uniform silicide coating which was mainly composed of NbSi2 and SiC and well bonded to the matrix was successfully formed on the surface of Nb4AlC3. The Si pack cemented Nb4AlC3 shows excellent oxidation resistance up to 1200 degrees C due to the formation of protective Al2O3 layer. The oxidation kinetics of the cemented Nb4AlC3 obey parabolic law all the way to up to 1200 degrees C, and the parabolic rate constants of cemented Nb4AlC3 are in the same order of magnitude as those of Ti3AlC2 in the temperature range 1000 degrees C-1200 degrees C. However, the oxidation of the cemented Nb4AlC3 was accelerated after oxidation at 1300 degrees C for about 15h due to the formation of NbAlO4.
description.department[zheng, liya ; wang, jingyang] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china. [zheng, liya] chinese acad sci, grad sch, beijing 100039, peoples r china. [zhou, yanchun] arimpt, sci & technol adv funct composite lab, beijing 100076, peoples r china. ; zhou, yc (reprint author), arimpt, sci & technol adv funct composite lab, 1 south dahongmen rd, beijing 100076, peoples r china. ; yczhou714@gmail.com
KeywordMechanical-properties Behavior Composites Protection Phases Air
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/72509
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
L. Y. Zheng,J. Y. Wang,Y. C. Zhou. Improving the High-Temperature Oxidation Resistance of Nb4AlC3 by Silicon Pack Cementation[J]. Journal of the American Ceramic Society,2014,97(2):552-561.
APA L. Y. Zheng,J. Y. Wang,&Y. C. Zhou.(2014).Improving the High-Temperature Oxidation Resistance of Nb4AlC3 by Silicon Pack Cementation.Journal of the American Ceramic Society,97(2),552-561.
MLA L. Y. Zheng,et al."Improving the High-Temperature Oxidation Resistance of Nb4AlC3 by Silicon Pack Cementation".Journal of the American Ceramic Society 97.2(2014):552-561.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[L. Y. Zheng]'s Articles
[J. Y. Wang]'s Articles
[Y. C. Zhou]'s Articles
Baidu academic
Similar articles in Baidu academic
[L. Y. Zheng]'s Articles
[J. Y. Wang]'s Articles
[Y. C. Zhou]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[L. Y. Zheng]'s Articles
[J. Y. Wang]'s Articles
[Y. C. Zhou]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.