Effect of sulphur dioxide on the corrosion of a low alloy steel in simulated coastal industrial atmosphere

IMR OpenIR

	Effect of sulphur dioxide on the corrosion of a low alloy steel in simulated coastal industrial atmosphere
	W. J. Chen; L. Hao; J. H. Dong; W. Ke
	2014
发表期刊	Corrosion Science
ISSN	0010-938X
卷号	83 页码:155-163
摘要	This investigation aims to study the effect of SO2 on the corrosion of a low alloy steel in simulated coastal industrial atmospheres. The results indicate that the corrosion weight gain of the steel firstly increases with increasing SO2 content to a certain level and then decreases with further increasing the SO2 content. Besides, higher SO2 content promotes the formation of alpha-FeOOH and inhibits the formation of gamma-FeOOH. Moreover, it seems that the deterioration effect of SO2 to steel corrosion is not obvious in the initial corrosion stage and SO2 begins to accelerate the steel corrosion as the corrosion process increases. 2014 Elsevier Ltd. All rights reserved.
部门归属	[chen, wenjuan ; hao, long ; dong, junhua ; ke, wei] chinese acad sci, state key lab corros & protect, inst met res, shenyang 110016, peoples r china. ; dong, jh (reprint author), chinese acad sci, state key lab corros & protect, inst met res, wencui rd 62, shenyang 110016, peoples r china. ; chinahaolong@126.com ; jhdong@imr.ac.cn
关键词	Low Alloy Steel Xrd Polarisation Eis Atmospheric Corrosion Rust Mncup Weathering Steel Carbon-steel Environments Iron Performance Resistance Mechanisms Evolution Exposure China
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/72833
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	W. J. Chen,L. Hao,J. H. Dong,et al. Effect of sulphur dioxide on the corrosion of a low alloy steel in simulated coastal industrial atmosphere[J]. Corrosion Science,2014,83:155-163.
APA	W. J. Chen,L. Hao,J. H. Dong,&W. Ke.(2014).Effect of sulphur dioxide on the corrosion of a low alloy steel in simulated coastal industrial atmosphere.Corrosion Science,83,155-163.
MLA	W. J. Chen,et al."Effect of sulphur dioxide on the corrosion of a low alloy steel in simulated coastal industrial atmosphere".Corrosion Science 83(2014):155-163.