Corrosion Behavior of X52 Anti-H2S Pipeline Steel Exposed to High H2S Concentration Solutions at 90 degrees C

IMR OpenIR

	Corrosion Behavior of X52 Anti-H2S Pipeline Steel Exposed to High H2S Concentration Solutions at 90 degrees C
	M. Liu; J. Q. Wang; W. Ke; E. H. Han
	2014
发表期刊	Journal of Materials Science & Technology
ISSN	1005-0302
卷号	30 期号:5 页码:504-510
摘要	Initial corrosion kinetics of X52 anti-H2S pipeline steel exposed to 90 degrees C/1.61 MPa H2S solutions was investigated through high temperature and high pressure immersion tests. Corrosion rates were obtained based on weight loss calculation. The corrosion products were analyzed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and electron probe micro-analysis (EPMA). The initial corrosion kinetics was found to obey the exponential law. With increasing immersion time, the main corrosion products changed from iron-rich mackinawite to sulfur-rich pyrrhotite. The corrosion films had two layers: an inner fine-grained layer rich in iron and an outer columnar-grained layer rich in sulfur. The corrosion film formed through the combination of outward diffusion of Fe2+ ions and inward diffusion of HS- ions. The variation of the corrosion products and compaction of the corrosion layer resulted in a decrease in the diffusion coefficient with increasing immersion time. The double-layered corrosion film formed after long time immersion acted as an effective barrier against diffusion.
部门归属	[liu, meng ; wang, jianqiu ; ke, wei ; han, en-hou] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; wang, jq (reprint author), chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; wangjianqiu@imr.ac.cn
关键词	H2s Corrosion X52 Anti-h2s Pipeline Steel High Temperature Iron Sulfide Hydrogen-sulfide Iron Morphology Diagrams
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/72880
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	M. Liu,J. Q. Wang,W. Ke,et al. Corrosion Behavior of X52 Anti-H2S Pipeline Steel Exposed to High H2S Concentration Solutions at 90 degrees C[J]. Journal of Materials Science & Technology,2014,30(5):504-510.
APA	M. Liu,J. Q. Wang,W. Ke,&E. H. Han.(2014).Corrosion Behavior of X52 Anti-H2S Pipeline Steel Exposed to High H2S Concentration Solutions at 90 degrees C.Journal of Materials Science & Technology,30(5),504-510.
MLA	M. Liu,et al."Corrosion Behavior of X52 Anti-H2S Pipeline Steel Exposed to High H2S Concentration Solutions at 90 degrees C".Journal of Materials Science & Technology 30.5(2014):504-510.