Evaluation of corrosion resistance of aluminium coating with and without annealing against molten carbonate using electrochemical impedance spectroscopy

IMR OpenIR

	Evaluation of corrosion resistance of aluminium coating with and without annealing against molten carbonate using electrochemical impedance spectroscopy
	C. S. Ni; L. Y. Lu; C. L. Zeng; Y. Niu
	2014
发表期刊	Journal of Power Sources
ISSN	0378-7753
卷号	261 页码:162-169
摘要	An arc ion plating (AIP) was used to fabricate a FeAl layer on 310S stainless steel to protect the sealing area being corroded by the molten carbonate in molten carbonate fuel cells (MCFCs). The degradation of aluminide coatings comes from both the corrosion of the coating in contact with the molten carbonate and the aluminium depletion due to the interdiffusion of aluminium and the substrate. The in-situ forming of aluminide in molten carbonate at 650 C could be a possible way to reduce the inward diffusion of aluminium in the conventional pre-annealing at 850 degrees C. Electrochemical impedance spectroscopy (EIS) measurements were performed to model the corrosion of this pre-formed FeAl coating in comparison with the one formed in-situ in molten (0.62 Li+038 K)(2)CO3 at 650 degrees C. Although alpha-LiAlO2 is the corrosion product in both cases, the impedance spectra show distinct rate-limiting steps; the former is controlled by the charged particles passing through the scale, while the latter by their diffusion in the melt. The microstructure of the scale might be the reason for the difference in corrosion mechanism. (C) 2014 Elsevier B.V. All rights reserved.
部门归属	[ni, c. s. ; lu, l. y. ; zeng, c. l. ; niu, y.] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; niu, y (reprint author), chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; yniu@imr.ac.cn
关键词	Stainless Steel Molten Salts Intermetallics Electrochemical Impedance Spectroscopy Hot Corrosion Wet-seal Area Surface Characterization Methods Bipolar Plate Materials Fuel-cells Intermetallic Alloy Separator Plates li+k Carbonate Hot Corrosion Behavior Oxygen
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/72893
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	C. S. Ni,L. Y. Lu,C. L. Zeng,et al. Evaluation of corrosion resistance of aluminium coating with and without annealing against molten carbonate using electrochemical impedance spectroscopy[J]. Journal of Power Sources,2014,261:162-169.
APA	C. S. Ni,L. Y. Lu,C. L. Zeng,&Y. Niu.(2014).Evaluation of corrosion resistance of aluminium coating with and without annealing against molten carbonate using electrochemical impedance spectroscopy.Journal of Power Sources,261,162-169.
MLA	C. S. Ni,et al."Evaluation of corrosion resistance of aluminium coating with and without annealing against molten carbonate using electrochemical impedance spectroscopy".Journal of Power Sources 261(2014):162-169.