Loss of mechanical properties in vivo and bone-implant interface strength of AZ31B magnesium alloy screws with Si-containing coating
L. L. Tan; Q. Wang; X. Lin; P. Wan; G. D. Zhang; Q. Zhang; K. Yang
2014
Source PublicationActa Biomaterialia
ISSN1742-7061
Volume10Issue:5Pages:2333-2340
AbstractIn this study the loss of mechanical properties and the interface strength of coated AZ31B magnesium alloy (a magnesium-aluminum alloy) screws with surrounding host tissues were investigated and compared with non-coated AZ31B, degradable polymer and biostable titanium alloy screws in a rabbit animal model after 1, 4, 12 and 21 weeks of implantation. The interface strength was evaluated in terms of the extraction torque required to back out the screws. The loss of mechanical properties over time was indicated by one-point bending load loss of the screws after these were extracted at different times. AZ31B samples with a silicon-containing coating had a decreased degradation rate and improved biological properties. The extraction torque of Ti6AI4V, poly-L-lactide (PLLA) and coated AZ31B increased significantly from 1 week to 4 weeks post-implantation, indicating a rapid osteosynthesis process over 3 weeks. The extraction torque of coated AZ31B increased with implantation time, and was higher than that of PLLA after 4 weeks of implantation, equalling that of Ti6AI4V at 12 weeks and was higher at 21 weeks. The bending loads of non-coated AZ31B and PLLA screws degraded sharply after implantation, and that of coated AZ31B degraded more slowly. The biodegradation mechanism, the coating to control the degradation rate and the bioactivity of magnesium alloys influencing the mechanical properties loss over time and bone-implant interface strength are discussed in this study and it is concluded that a suitable degradation rate will result in an improvement in the mechanical performance of magnesium alloys, making them more suitable for clinical application. (C) 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
description.department[tan, lili ; wang, qiang ; lin, xiao ; wan, peng ; yang, ke] chinese acad sci, inst met res, shenyang 110016, peoples r china. [wang, qiang ; zhang, guangdao] china med univ, sch stomatol, shenyang 110002, peoples r china. [zhang, qiang] gen hosp peoples liberat army, dept orthopaed, beijing 100853, peoples r china. ; tan, ll (reprint author), chinese acad sci, inst met res, 72 wenhua rd, shenyang 110016, peoples r china. ; lltan@imr.ac.cn ; kyang@imr.ac.cn
KeywordMagnesium Alloy Si-containing Coating Mechanical Properties Loss Bone-implant Interface Strength Degradation Behavior Mg Electrodeposition Hydroxyapatite Performance Silicon Vitro
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/72911
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
L. L. Tan,Q. Wang,X. Lin,et al. Loss of mechanical properties in vivo and bone-implant interface strength of AZ31B magnesium alloy screws with Si-containing coating[J]. Acta Biomaterialia,2014,10(5):2333-2340.
APA L. L. Tan.,Q. Wang.,X. Lin.,P. Wan.,G. D. Zhang.,...&K. Yang.(2014).Loss of mechanical properties in vivo and bone-implant interface strength of AZ31B magnesium alloy screws with Si-containing coating.Acta Biomaterialia,10(5),2333-2340.
MLA L. L. Tan,et al."Loss of mechanical properties in vivo and bone-implant interface strength of AZ31B magnesium alloy screws with Si-containing coating".Acta Biomaterialia 10.5(2014):2333-2340.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[L. L. Tan]'s Articles
[Q. Wang]'s Articles
[X. Lin]'s Articles
Baidu academic
Similar articles in Baidu academic
[L. L. Tan]'s Articles
[Q. Wang]'s Articles
[X. Lin]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[L. L. Tan]'s Articles
[Q. Wang]'s Articles
[X. Lin]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.