Comparison of Corrosion Resistance of UNS N06690TT and UNS N08800SN in Simulated Primary Water with Various Concentrations of Dissolved Oxygen
J. Q. Wang; X. H. Li; F. Huang; Z. M. Zhang; J. Z. Wang; R. W. Staehle
2014
Source PublicationCorrosion
ISSN0010-9312
Volume70Issue:6Pages:598-614
AbstractCorrosion behaviors of UNS N06690TT and N08800SN in simulated pressurized water reactor (PWR) primary water containing three concentrations of dissolved oxygen (DO) was studied by open-circuit potential (OCP), electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), x-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). These results have shown that DO in simulated PWR primary water produces a strong effect on Cr dissolution. At DO < 0.01 ppm, the electrochemical impedance of N06690TT at low frequency gradually increases and becomes larger than that of N08800SN, and N06690TT shows slightly better corrosion resistance than N08800SN. At DO 0.1 ppm, the electrochemical impedance of N06690TT at low frequency rapidly decreases and becomes lower than that of N08800SN with the increase of immersion time; N08800SN shows much better corrosion resistance than N06690TT. The spinet oxides NiFe2O4 or Fe3O4 can form in the inner oxide layer on N08800SN due to relatively balanced ratio of Fe, Ni, which leads to the relatively stable corrosion resistance. Therefore, when DO in PWR primary water is 0.1 ppm or more, it is more suitable to choose N08800SN rather than N06690TT as the steam generator (SG) tubing materials.
description.department[wang, jianqiu ; li, xiaohui ; huang, fa ; zhang, zhiming ; wang, jiazhen] chinese acad sci, state key lab corros & protect, inst met res, shenyang 110016, liaoning, peoples r china. [li, xiaohui] state nucl power plant serv co, shanghai 200233, peoples r china. [staehle, roger w.] staehle consulting, st paul, mn usa. ; wang, jq (reprint author), chinese acad sci, state key lab corros & protect, inst met res, shenyang 110016, liaoning, peoples r china. ; wangjianqiu@imr.ac.cn
KeywordDissolved Oxygen Electrochemical Impedance Spectroscopy Pressurized Water Reactor Primary Water Uns N06690 Uns N08800 High-temperature Alloy 690 Dissolution Behavior Cracking Reactor Films
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/72916
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
J. Q. Wang,X. H. Li,F. Huang,et al. Comparison of Corrosion Resistance of UNS N06690TT and UNS N08800SN in Simulated Primary Water with Various Concentrations of Dissolved Oxygen[J]. Corrosion,2014,70(6):598-614.
APA J. Q. Wang,X. H. Li,F. Huang,Z. M. Zhang,J. Z. Wang,&R. W. Staehle.(2014).Comparison of Corrosion Resistance of UNS N06690TT and UNS N08800SN in Simulated Primary Water with Various Concentrations of Dissolved Oxygen.Corrosion,70(6),598-614.
MLA J. Q. Wang,et al."Comparison of Corrosion Resistance of UNS N06690TT and UNS N08800SN in Simulated Primary Water with Various Concentrations of Dissolved Oxygen".Corrosion 70.6(2014):598-614.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[J. Q. Wang]'s Articles
[X. H. Li]'s Articles
[F. Huang]'s Articles
Baidu academic
Similar articles in Baidu academic
[J. Q. Wang]'s Articles
[X. H. Li]'s Articles
[F. Huang]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[J. Q. Wang]'s Articles
[X. H. Li]'s Articles
[F. Huang]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.