题名: Ti60合金近β锻造后微观断口形貌研究
作者: 郭真真;  曾卫东;  朱艳春;  俞汉清;  王清江
发表日期: 2013-9-25
摘要: 采用光学显微镜和扫描电子显微镜观察了Ti60合金近β锻造后的显微组织和室温拉伸试样、热稳定试样的断口形貌并确定断裂方式。结果表明:Ti60合金采用近β锻造,获得三态组织;室温拉伸试样断口裂纹源起源于试样中心,断面凹凸不平,既有韧窝形貌又有解理断裂特征,为混合型断口;热稳定试样断口裂纹源位于试样边缘,断口表面平整,为典型的解理断裂特征;试样经热暴露后,强度变化不大,塑性明显降低。
刊名: 材料导报
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
郭真真,曾卫东,朱艳春,等. Ti60合金近β锻造后微观断口形貌研究[J]. 材料导报,2013(18):112-114+121.
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [郭真真]'s Articles
 [曾卫东]'s Articles
 [朱艳春]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [郭真真]‘s Articles
 [曾卫东]‘s Articles
 [朱艳春]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2016  中国科学院金属研究所  -Feedback
Powered by CSpace