Effects of grain size on the high-cycle fatigue behavior of IN792 superalloy
B. N. Du; J. X. Yang; C. Y. Cui; X. F. Sun
2015
Source PublicationMaterials & Design
ISSN0261-3069
Volume65Pages:57-64
AbstractThe HCF (high-cycle fatigue) property of Ni-base cast superalloy IN792 with various grain sizes was investigated at 700 degrees C, 800 degrees C and 900 degrees C. The results show that grain refinement could improve the HCF lives since it could reduce the probability that "fatigue hot spots'' initiate near the surface. The improvement effect of grain refinement on the HCF life decreases with the increase of temperature and applied loading amplitude due to that the increasing of temperature and applied loading amplitude would cause a transition of "fatigue hot spots'' from the bulk to the surface or subsurface for fine grain specimens. The HCF deformation mechanism was studied through dislocation structure observation. At 700 degrees C, the movement of dislocations is restricted in the slip bands and the fatigue cracks form in a glide plane decohension manner, therefore it is easier to generate a fatigue crack for coarse grain specimens than fine grain specimens. As the temperature increased to 800 degrees C and 900 degrees C, the distribution of dislocations become more homogeneous and glide plane decohension is inhibited, so that the role of grain refinement on the HCF behavior is decreased. (C) 2014 Elsevier Ltd. All rights reserved.
description.department[du, beining ; yang, jinxia ; cui, chuanyong ; sun, xiaofeng] chinese acad sci, inst met res, shenyang 110016, peoples r china. ; cui, cy (reprint author), chinese acad sci, inst met res, 72 wenhua rd, shenyang 110016, peoples r china. ; chycui@imr.ac.cn
KeywordNickel Super Alloy Grain Refinement High Cycle Fatigue Nickel-base Superalloy Elevated-temperatures Crack-growth Mechanical-properties Tensile Properties Microstructure Initiation Deformation Character 713lc
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/73215
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
B. N. Du,J. X. Yang,C. Y. Cui,et al. Effects of grain size on the high-cycle fatigue behavior of IN792 superalloy[J]. Materials & Design,2015,65:57-64.
APA B. N. Du,J. X. Yang,C. Y. Cui,&X. F. Sun.(2015).Effects of grain size on the high-cycle fatigue behavior of IN792 superalloy.Materials & Design,65,57-64.
MLA B. N. Du,et al."Effects of grain size on the high-cycle fatigue behavior of IN792 superalloy".Materials & Design 65(2015):57-64.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[B. N. Du]'s Articles
[J. X. Yang]'s Articles
[C. Y. Cui]'s Articles
Baidu academic
Similar articles in Baidu academic
[B. N. Du]'s Articles
[J. X. Yang]'s Articles
[C. Y. Cui]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[B. N. Du]'s Articles
[J. X. Yang]'s Articles
[C. Y. Cui]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.