Observation of etch pits in Fe-36wt%Ni Invar alloy
D. Z. Lu; M. J. Wu
2014
Source PublicationInternational Journal of Minerals Metallurgy and Materials
ISSN1674-4799
Volume21Issue:7Pages:682-686
AbstractTo indirectly investigate the dislocation behavior of Fe-36wt%Ni Invar alloy by the etch pit method, polished Invar specimens were etched by a solution containing 4 g copper sulfate, 20 mL hydrochloric acid, and 20 mL deionized water for 2 min. Etch pits in the etched surfaces were observed. All the etch pits in one specific grain exhibited similar shapes, which are closely related to the grain orientations. These etch pits were characterized as dislocation etch pits. It was observed that etch pits arranged along grain boundaries, gathered at grain tips and strip-like etch pit clusters passed through a number of grains in the pure Invar specimens. After the addition of a small amount of alloying elements, the identification of a single dislocation etch pit is challenging compared with the pure Invar alloy. Thus, the observation of etch pits facilitates the investigation on the dislocation behavior of the pure Invar alloy. In addition, alloying elements may affect the densities and sizes of etch pits.
description.department[lu, dong-zhu ; wu, min-jie] chinese acad sci, inst met res, div surface engn mat, shenyang 110016, peoples r china. ; lu, dz (reprint author), chinese acad sci, inst met res, div surface engn mat, shenyang 110016, peoples r china. ; dzlu11b@imr.ac.cn
KeywordInvar Alloy Dislocations Etch Pit Technique Alloying Elements Dislocation Density Gan Reduction
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/73325
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
D. Z. Lu,M. J. Wu. Observation of etch pits in Fe-36wt%Ni Invar alloy[J]. International Journal of Minerals Metallurgy and Materials,2014,21(7):682-686.
APA D. Z. Lu,&M. J. Wu.(2014).Observation of etch pits in Fe-36wt%Ni Invar alloy.International Journal of Minerals Metallurgy and Materials,21(7),682-686.
MLA D. Z. Lu,et al."Observation of etch pits in Fe-36wt%Ni Invar alloy".International Journal of Minerals Metallurgy and Materials 21.7(2014):682-686.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[D. Z. Lu]'s Articles
[M. J. Wu]'s Articles
Baidu academic
Similar articles in Baidu academic
[D. Z. Lu]'s Articles
[M. J. Wu]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[D. Z. Lu]'s Articles
[M. J. Wu]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.