Correlation Between Microstructure and Corrosion Behavior of Two 90Cu10Ni Alloy Tubes
A. L. Ma; S. L. Jiang; Y. G. Zheng; Z. M. Yao; W. Ke; S. Xia
2014
Source PublicationActa Metallurgica Sinica-English Letters
ISSN1006-7191
Volume27Issue:4Pages:730-738
AbstractTwo kinds of 90Cu10Ni tubes with different service lives (more than 3 years and only 1 year, respectively) under identical working conditions were studied by an immersion test in a 3.5 wt% NaCl solution and the electron backscattered diffraction (EBSD) technique. The morphology after immersion showed severer corrosion attack at the grain boundaries of the tube with shorter service life compared with the tube with longer service life. The grain boundary characterization distributions (GBCDs) of the two tubes obtained by EBSD revealed more Sigma 3 boundaries and twins, and larger random boundary meshes in the tube with longer service life. A short immersion test in a modified Livingston's solution was conducted to evaluate the tendency to corrosion attack of different types of the grain boundaries. SEM and AFM were used to characterize the corrosion morphologies of the boundaries. A strong correlation between varying depths of corrosion grooves and types of the grain boundaries was obtained. The influence of deviation angle of low Sigma boundaries on corrosion resistance of the grain boundaries was also discussed. It is concluded that a special "grain boundary engineering" (GBE) treatment has been performed on the tube with longer service life. It is proposed that the optimized GBCD is responsible for the better service performance of the tube.
description.department[ma, aili ; jiang, shengli ; zheng, yugui ; yao, zhiming ; ke, wei] chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, peoples r china. [xia, shuang] shanghai univ, inst mat, shanghai 200072, peoples r china. ; zheng, yg (reprint author), chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, peoples r china. ; ygzheng@imr.ac.cn
Keyword90cu10ni Alloy Corrosion Resistance Grain Boundary Twin Sigma 3 Boundary Electron Backscattered Diffraction Grain-boundary-character Austenitic Stainless-steel Cu-ni Alloys Intergranular Corrosion Pure Copper Sea-water Seawater Plane Nickel Resistance
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/73336
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
A. L. Ma,S. L. Jiang,Y. G. Zheng,et al. Correlation Between Microstructure and Corrosion Behavior of Two 90Cu10Ni Alloy Tubes[J]. Acta Metallurgica Sinica-English Letters,2014,27(4):730-738.
APA A. L. Ma,S. L. Jiang,Y. G. Zheng,Z. M. Yao,W. Ke,&S. Xia.(2014).Correlation Between Microstructure and Corrosion Behavior of Two 90Cu10Ni Alloy Tubes.Acta Metallurgica Sinica-English Letters,27(4),730-738.
MLA A. L. Ma,et al."Correlation Between Microstructure and Corrosion Behavior of Two 90Cu10Ni Alloy Tubes".Acta Metallurgica Sinica-English Letters 27.4(2014):730-738.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[A. L. Ma]'s Articles
[S. L. Jiang]'s Articles
[Y. G. Zheng]'s Articles
Baidu academic
Similar articles in Baidu academic
[A. L. Ma]'s Articles
[S. L. Jiang]'s Articles
[Y. G. Zheng]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[A. L. Ma]'s Articles
[S. L. Jiang]'s Articles
[Y. G. Zheng]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.