In Situ Corrosion Monitoring of Mild Steel in a Simulated Tidal Zone without Marine Fouling Attachment by Electrochemical Impedance Spectroscopy

IMR OpenIR

	In Situ Corrosion Monitoring of Mild Steel in a Simulated Tidal Zone without Marine Fouling Attachment by Electrochemical Impedance Spectroscopy
	X. Mu; J. Wei; J. H. Dong; W. Ke
	2014
发表期刊	Journal of Materials Science & Technology
ISSN	1005-0302
卷号	30 期号:10 页码:1043-1050
摘要	The corrosion behaviors of the isolated short and vertical long scale Q235B steel in a simulated tidal zone were studied by electrochemical impedance spectroscopy (EIS) monitoring and corrosion weight loss calculation in an experimental indoor simulating trough. The results show that the corrosion rate of the isolated short scale Q235B steel in the tidal zone acquired by the EIS agrees with the corrosion weight loss result. The corrosion rates of the short scale steel are in the order of middle tidal zone > the central zone between the middle tidal zone and low tidal zone > high tidal zone > low tidal zone. The fastest corrosion rate in the middle tidal zone is attributed to the longest wet time in a tidal cycle. According to the comparison of corrosion weight loss between the vertical long scale and isolated short scale specimens, the corrosion rate of vertical long scale specimens of Q235B steel is lower than that of the isolated short scale specimens in the tidal zone, but the result is contrary in the immersion zone.
部门归属	[mu, xin ; wei, jie ; dong, junhua ; ke, wei] chinese acad sci, state key lab corros & protect, inst met res, shenyang 110016, peoples r china. ; dong, jh (reprint author), chinese acad sci, state key lab corros & protect, inst met res, shenyang 110016, peoples r china. ; jhdong@imr.ac.cn
关键词	Laboratory Simulation Tidal Corrosion Mild Steel Electrochemical Impedance Spectroscopy Weight Loss Wet-dry Conditions Atmospheric Corrosion Environment
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/73345
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	X. Mu,J. Wei,J. H. Dong,et al. In Situ Corrosion Monitoring of Mild Steel in a Simulated Tidal Zone without Marine Fouling Attachment by Electrochemical Impedance Spectroscopy[J]. Journal of Materials Science & Technology,2014,30(10):1043-1050.
APA	X. Mu,J. Wei,J. H. Dong,&W. Ke.(2014).In Situ Corrosion Monitoring of Mild Steel in a Simulated Tidal Zone without Marine Fouling Attachment by Electrochemical Impedance Spectroscopy.Journal of Materials Science & Technology,30(10),1043-1050.
MLA	X. Mu,et al."In Situ Corrosion Monitoring of Mild Steel in a Simulated Tidal Zone without Marine Fouling Attachment by Electrochemical Impedance Spectroscopy".Journal of Materials Science & Technology 30.10(2014):1043-1050.