Wear and corrosion behavior of Mg-Gd-Y-Zr alloy treated by mixed molten-salt bath

IMR OpenIR

	Wear and corrosion behavior of Mg-Gd-Y-Zr alloy treated by mixed molten-salt bath
	Y. S. Niu; R. H. Cui; Y. T. He; Z. M. Yu
	2014
发表期刊	Journal of Alloys and Compounds
ISSN	0925-8388
卷号	610 页码:294-300
摘要	A novel kind of oxide film was successfully prepared on the Mg-Gd-Y-Zr alloy by mixed molten-salt bath treatment. The composition and microstructure of the film were studied by XRD and SEM. Wear and corrosion behavior of the modified surface film was evaluated. According to XRD and SEM analysis, it was confirmed that the oxide film resulted in uniform distribution of MgO phase. The implantation of MgO phase in the film is expected to harden the surface and retard the dissolution behavior greatly in NaCl solution, and acts as an artificial compact and continuous passive film with the thickness of tens of microns. (C) 2014 Elsevier B.V. All rights reserved.
部门归属	[niu, yunsong ; yu, zhiming] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. [cui, ronghong ; he, yuting] air force engn univ, aeronaut & astronaut engn coll, xian 710038, peoples r china. ; niu, ys (reprint author), chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; ysniu@imr.ac.cn
关键词	Magnesium Eis Wear Corrosion Oxide Coatings Az91d Magnesium Alloy Conversion Coatings Impedance Spectroscopy Microarc Oxidation Carbon-steel Resistance Surface Films Az31 Temperature
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/73351
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Y. S. Niu,R. H. Cui,Y. T. He,et al. Wear and corrosion behavior of Mg-Gd-Y-Zr alloy treated by mixed molten-salt bath[J]. Journal of Alloys and Compounds,2014,610:294-300.
APA	Y. S. Niu,R. H. Cui,Y. T. He,&Z. M. Yu.(2014).Wear and corrosion behavior of Mg-Gd-Y-Zr alloy treated by mixed molten-salt bath.Journal of Alloys and Compounds,610,294-300.
MLA	Y. S. Niu,et al."Wear and corrosion behavior of Mg-Gd-Y-Zr alloy treated by mixed molten-salt bath".Journal of Alloys and Compounds 610(2014):294-300.