Role of TiN inclusion on corrosion fatigue behavior of Alloy 690 steam generator tubes in borated and lithiated high temperature water
J. B. Tan; X. Q. Wu; E. H. Han; W. Ke; X. Q. Liu; F. J. Meng; X. L. Xu
2014
Source PublicationCorrosion Science
ISSN0010-938X
Volume88Pages:349-359
AbstractInfluence of TiN inclusion on corrosion fatigue behavior of three types of as-received Alloy 690 steam generator tubes (J, C1 and C2) in borated and lithiated high temperature water was investigated. The volume fraction of inclusions in tube J, C1 and C2 were about 0.0894%, 0.0384% and 0.1843%. The fatigue life of tube C2 was slightly shorter than that of tube J and C1. Large broken TiN inclusions and TiN-inclusion clusters played a significant role on fatigue crack initiation and propagation for tube C2 in high temperature water. The inclusion-involved fatigue cracking mechanisms are discussed. (C) 2014 Elsevier Ltd. All rights reserved.
description.department[tan, jibo] univ sci & technol china, hefei 230000, peoples r china. [tan, jibo ; wu, xinqiang ; han, en-hou ; ke, wei] chinese acad sci, key lab nucl mat & safety assessment, liaoning key lab safety & assessment tech nucl ma, inst met res, shenyang 110016, peoples r china. [liu, xiaoqiang ; meng, fanjiang ; xu, xuelian] shanghai nucl engn res & design inst, shanghai 200233, peoples r china. ; wu, xq (reprint author), chinese acad sci, key lab nucl mat & safety assessment, liaoning key lab safety & assessment tech nucl ma, inst met res, shenyang 110016, peoples r china. ; xqwu@imr.ac.cn
KeywordAlloy Sem Corrosion Fatigue High Temperature Corrosion Inclusion Non-metallic Inclusions Pressure-vessel Steel High-strength Steels Low-cycle Fatigue Stainless-steel Nickel-alloys Crack-growth Quantitative-evaluation Dissolved-oxygen Hydrogen
URL查看原文
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/73383
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
J. B. Tan,X. Q. Wu,E. H. Han,et al. Role of TiN inclusion on corrosion fatigue behavior of Alloy 690 steam generator tubes in borated and lithiated high temperature water[J]. Corrosion Science,2014,88:349-359.
APA J. B. Tan.,X. Q. Wu.,E. H. Han.,W. Ke.,X. Q. Liu.,...&X. L. Xu.(2014).Role of TiN inclusion on corrosion fatigue behavior of Alloy 690 steam generator tubes in borated and lithiated high temperature water.Corrosion Science,88,349-359.
MLA J. B. Tan,et al."Role of TiN inclusion on corrosion fatigue behavior of Alloy 690 steam generator tubes in borated and lithiated high temperature water".Corrosion Science 88(2014):349-359.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[J. B. Tan]'s Articles
[X. Q. Wu]'s Articles
[E. H. Han]'s Articles
Baidu academic
Similar articles in Baidu academic
[J. B. Tan]'s Articles
[X. Q. Wu]'s Articles
[E. H. Han]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[J. B. Tan]'s Articles
[X. Q. Wu]'s Articles
[E. H. Han]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.