| Friction stir welding of as-extruded Mg-Al-Zn alloy with higher Al content. Part II: Influence of precipitates | |
| J. Yang; D. R. Ni; D. Wang; B. L. Xiao; Z. Y. Ma | |
| 2014 | |
| Source Publication | Materials Characterization
 |
| ISSN | 1044-5803 |
| Volume | 96Pages:135-141 |
| Abstract | Extruded Mg-Al-Zn (AZ80) plates were subjected to friction stir welding at a welding speed of 100 min.min(-1) and a tool rotation rates of 800 rpm. Different heat treatments were conducted before or after welding with the aim to evaluate the influence of precipitates on the weld properties. The welding joint with the solution treatment before welding exhibited enhanced ductility and decreased yield strength due to the dissolution of beta-Mg17Al12 and the coarsening of grains. After aging at 180 degrees C for 16 h, a banded structure consisting of different densities of discontinuous beta-Mg17Al12 precipitates was observed in the nugget zone of both joints with or without the solution treatment before welding. The yield strength of the joint without the solution before welding increased by 30% after aging, with the elongation being decreased. The fracture behavior of the aged joints was closely related to the banded structure where the crack propagated more easily along the coarse discontinuously precipitated bands. (C) 2014 Elsevier Inc. All rights reserved. |
| description.department | [yang, j. ; ni, d. r. ; wang, d. ; xiao, b. l. ; ma, z. y.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. ; ma, zy (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, 72 wenhua rd, shenyang 110016, peoples r china. ; zyma@imr.ac.cn |
| Keyword | Magnesium Alloys Friction Stir Welding Banded Structure Heat Treatment Mechanical Properties Az91 Magnesium Alloy Welded Zk60 Alloy Mechanical-properties Microstructural Evolution Grain-size Fracture-behavior Texture Parameters Aluminum Az31b |
| URL | 查看原文 |
| Language | 英语 |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/73467 |
| Collection | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | J. Yang,D. R. Ni,D. Wang,et al. Friction stir welding of as-extruded Mg-Al-Zn alloy with higher Al content. Part II: Influence of precipitates[J]. Materials Characterization,2014,96:135-141. |
| APA | J. Yang,D. R. Ni,D. Wang,B. L. Xiao,&Z. Y. Ma.(2014).Friction stir welding of as-extruded Mg-Al-Zn alloy with higher Al content. Part II: Influence of precipitates.Materials Characterization,96,135-141. |
| MLA | J. Yang,et al."Friction stir welding of as-extruded Mg-Al-Zn alloy with higher Al content. Part II: Influence of precipitates".Materials Characterization 96(2014):135-141. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment