	Finite element and experimental studies of the formation mechanism of edge defects during machining of SiCp/Al composites
	L. Zhou; Y. Wang; Z. Y. Ma; X. L. Yu
	2014
发表期刊	International Journal of Machine Tools & Manufacture
ISSN	0890-6955
卷号	84 页码:9-16
摘要	In this paper, a multi-particle microfinite element model with a random particle distribution in SiCp/Al composites was developed using ABAQUS software. The formation mechanism of edge defects near the exit of orthogonal cutting was analyzed, and the effects of cutting parameters on the sizes of edge defects were investigated. The results indicate that both the brittle fracture of SiC particles and the plastic flow of Al matrix occur in the process of the edge defects formation. Additionally, the cutting speed has little effect on the sizes of edge defects but the cutting depth has a significant effect on the height and length of edge defects. The numerical results were also compared to the orthogonal cutting experimental data and found to be in reasonable agreement. (C) 2014 Elsevier Ltd. All rights reserved.
部门归属	[zhou, l. ; wang, y. ; yu, x. l.] shenyang ligong univ, sch mech engn, shenyang 110159, peoples r china. [ma, z. y.] chinese acad sci, inst met res, shenyang 110016, peoples r china. ; ma, zy (reprint author), chinese acad sci, inst met res, shenyang 110016, peoples r china. ; zyma@imr.ac.cn
关键词	Sicp/al Composites Formation Mechanism Edge Defects Orthogonal Cutting Experiment Finite Element Reinforced Plastic Composites Burr Formation Processes Metal-matrix Composites Feed Direction Exit Delamination Ceramics Reduction
URL	查看原文
语种	英语
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/73521
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	L. Zhou,Y. Wang,Z. Y. Ma,et al. Finite element and experimental studies of the formation mechanism of edge defects during machining of SiCp/Al composites[J]. International Journal of Machine Tools & Manufacture,2014,84:9-16.
APA	L. Zhou,Y. Wang,Z. Y. Ma,&X. L. Yu.(2014).Finite element and experimental studies of the formation mechanism of edge defects during machining of SiCp/Al composites.International Journal of Machine Tools & Manufacture,84,9-16.
MLA	L. Zhou,et al."Finite element and experimental studies of the formation mechanism of edge defects during machining of SiCp/Al composites".International Journal of Machine Tools & Manufacture 84(2014):9-16.