Enhancement the Adhesion between Epoxy Coating and Rusted Structural Steel by Tannic Acid Treatment
Y.; Ma Li, Y. T.; Zhang, B.; Lei, B.; Li, Y.
2014
Source PublicationActa Metallurgica Sinica-English Letters
ISSN1006-7191
Volume27Issue:6Pages:1105-1113
AbstractAn eco-friendly rust converter treatment based on tannic acid was optimized by orthogonal experiment, and the adhesion of the epoxy top-coating system was evaluated. The results showed that the adhesion between the epoxy coating and the rusted steel after treatment was enhanced from 1.93 to 5.97 MPa. This adhesion improvement was attributed to the formation of the micro-cracked tannic conversion layer and the increase of the compactness of the rust layer. The failure analysis suggested that the remainder rust was still the key issue for the further adhesion improvement of the coating system.
description.department[li, yang ; ma, yuantai ; zhang, bin ; lei, bing ; li, ying] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; li, y (reprint author), chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. ; liying@imr.ac.cn
KeywordTannic Acid Rust Adhesion Orthogonal Experiment Sem Ftir Corrosion Products Mangrove Tannins Metallic Iron Spectroscopy Converter Temperature Performance
URL查看原文
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/73850
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Y.,Ma Li, Y. T.,Zhang, B.,et al. Enhancement the Adhesion between Epoxy Coating and Rusted Structural Steel by Tannic Acid Treatment[J]. Acta Metallurgica Sinica-English Letters,2014,27(6):1105-1113.
APA Y.,Ma Li, Y. T.,Zhang, B.,Lei, B.,&Li, Y..(2014).Enhancement the Adhesion between Epoxy Coating and Rusted Structural Steel by Tannic Acid Treatment.Acta Metallurgica Sinica-English Letters,27(6),1105-1113.
MLA Y.,et al."Enhancement the Adhesion between Epoxy Coating and Rusted Structural Steel by Tannic Acid Treatment".Acta Metallurgica Sinica-English Letters 27.6(2014):1105-1113.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Y.]'s Articles
[Ma Li, Y. T.]'s Articles
[Zhang, B.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Y.]'s Articles
[Ma Li, Y. T.]'s Articles
[Zhang, B.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Y.]'s Articles
[Ma Li, Y. T.]'s Articles
[Zhang, B.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.