Recrystallisation nucleation of nickel base single crystal superalloy under compression
J.; Wang Meng, L.; Jin, T.; Sun, X. F.; Hu, Z. Q.
2014
Source PublicationMaterials Research Innovations
ISSN1432-8917
Volume18Pages:435-437
AbstractRecrystallisation nucleation of a nickel base single crystal superalloy cold deformed by compression and annealed at various temperatures has been investigated. The specimens were compressed using universal testing machine under an initial strain rate of 5x10(-4) s(-1) at room temperature. Annealing temperatures were chosen from 1100 to 1300 degrees C. The microstructure changes of the deformed and annealed samples were observed by optical microscopy, SEM with electron backscatter diffraction and TEM. It has been found that the surface and dendritic core are the preferential nucleation sites of recrystallised nucleus. The surface may lead to dislocation loss and relaxation of long range stresses, which will induce the recrystallised grains. At the dendritic core, rapid dissolution of gamma' particles during annealing reduces the resistance of grain boundary migration. Nucleation by low angle boundary migration and bow was confirmed during the recrystallisation of nickel base single crystal superalloy.
description.department[meng, j. ; wang, l. ; jin, t. ; sun, x. f. ; hu, z. q.] chinese acad sci, inst met res, dept superalloy, shenyang 110016, peoples r china. ; meng, j (reprint author), chinese acad sci, inst met res, dept superalloy, 72 wenhua rd, shenyang 110016, peoples r china. ; jmeng@imr.ac.cn
KeywordNickel Base Single Crystal Superalloy Recrystallisation Nucleation Behavior
URL查看原文
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/73887
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
J.,Wang Meng, L.,Jin, T.,et al. Recrystallisation nucleation of nickel base single crystal superalloy under compression[J]. Materials Research Innovations,2014,18:435-437.
APA J.,Wang Meng, L.,Jin, T.,Sun, X. F.,&Hu, Z. Q..(2014).Recrystallisation nucleation of nickel base single crystal superalloy under compression.Materials Research Innovations,18,435-437.
MLA J.,et al."Recrystallisation nucleation of nickel base single crystal superalloy under compression".Materials Research Innovations 18(2014):435-437.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[J.]'s Articles
[Wang Meng, L.]'s Articles
[Jin, T.]'s Articles
Baidu academic
Similar articles in Baidu academic
[J.]'s Articles
[Wang Meng, L.]'s Articles
[Jin, T.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[J.]'s Articles
[Wang Meng, L.]'s Articles
[Jin, T.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.