Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States

IMR OpenIR

	Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States
	Z. M.; Wang Zhang, J. Q.; Han, E. H.; Ke, W.
	2014
发表期刊	Journal of Materials Science & Technology
ISSN	1005-0302
卷号	30 期号:12 页码:1181-1192
摘要	Oxidation of Alloy 690TT samples either manually ground to 400 and 1500 grit, mechanically polished, or electropolished was performed in a solution of 1500 x 10(-6) B and 2.3 x 10(-6) Li with 2.5 x 10(-6) dissolved H-2, at 325 degrees C and 15.6 MPa for 60 days. The oxide films grown on samples with different surface states were analyzed using various techniques. Results show that a triple-layered structure was formed after immersion: an outermost layer with large scattered oxide particles rich in Fe and Ni, an intermediate layer with small compact oxide particles rich in Cr and Fe for the ground surfaces and loose needle-like oxides rich in Ni for the polished surfaces, and an inner layer with continuous Cr-rich oxides. The surface state was found to affect not only the surface morphology, but also the corrosion rate. Grinding accelerated the growth of protective oxide films such that the ground samples showed a lower oxidation rate than the polished ones. Samples of ground Alloy 690TT showed superior resistance to intergranular attack (IGA).
部门归属	[zhang, zhiming ; wang, jianqiu ; han, en-hou ; ke, wei] chinese acad sci, inst met res, liaoning key lab safety & assessment tech nucl ma, key lab nucl mat & safety assessment, shenyang 110016, peoples r china. ; wang, jq (reprint author), chinese acad sci, inst met res, liaoning key lab safety & assessment tech nucl ma, key lab nucl mat & safety assessment, shenyang 110016, peoples r china. ; wangjianqiu@imr.ac.cn
关键词	Alloy 690tt Oxidation Surface States High Pressure And High Temperature High-temperature Water Stress-corrosion Cracking Nickel-based Alloys Type-316 Stainless-steel Mixed-conduction Model X-ray Photoelectron Fe-cr Alloys Supercritical Water 288-degrees-c Water Electrochemical-behavior
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/74032
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Z. M.,Wang Zhang, J. Q.,Han, E. H.,et al. Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States[J]. Journal of Materials Science & Technology,2014,30(12):1181-1192.
APA	Z. M.,Wang Zhang, J. Q.,Han, E. H.,&Ke, W..(2014).Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States.Journal of Materials Science & Technology,30(12),1181-1192.
MLA	Z. M.,et al."Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States".Journal of Materials Science & Technology 30.12(2014):1181-1192.