Oxidation protection of carbon/carbon composites with a plasma-sprayed ZrB2-SiC-Si/Yb2SiO5/LaMgAal(11)O(19) coating during thermal cycling
B. L.; Hui Zou, Y.; Huang, W. Z.; Zhao, S. M.; Chen, X. L.; Xu, R. Y.; Tao, S. Y.; Wang, Y.; Cai, X. L.; Cao, X. Q.
2015
Source PublicationJournal of the European Ceramic Society
ISSN0955-2219
Volume35Issue:7Pages:2017-2025
AbstractCarbon/carbon composites were plasma sprayed with a ZrB2-SiC-Si/Yb2SiO5/LaMgAl11O9 coating to improve the oxidation resistance at high temperature. Oxidation protection behavior of the coating was investigated by thermal cycling test using a gas flame about 2273 K. Results showed that the weight loss for the completely coated sample was only 0.30% after 10 cycles of heating for 79 min, and it gradually increased to 4.8% until the failure of coating with 24 cycles. The presence of through-cracks and horizontal cracks in the coating due to the durative oxidation of ZrB2-SiC-Si layer progressively accelerated the oxidation of substrate and failure of coating. (C) 2015 Elsevier Ltd. All rights reserved.
description.department[zou, binglin ; hui, yu ; huang, wenzhi ; zhao, sumei ; chen, xiaolong ; xu, raying ; wang, ying ; cai, xiaolong ; cao, xueqiang] chinese acad sci, changchun inst appl chem, state key lab rare earth resources utilizat, changchun 130022, peoples r china. [zou, binglin ; tao, shunyan] chinese acad sci, shanghai inst ceram, key lab inorgan coating mat, shanghai 200050, peoples r china. [chen, xiaolong] chinese acad sci, inst met res, shenyang 110016, peoples r china. [huang, wenzhi] natl univ def technol, sci & technol adv ceram fibers & composites lab, changsha 410073, hunan, peoples r china. ; chen, xl (reprint author), chinese acad sci, changchun inst appl chem, state key lab rare earth resources utilizat, renmin st 5625, changchun 130022, peoples r china. ; xlchen@imnac.cn ; xcao@ciac.ac.cn
KeywordCarbon/carbon Composites Coating Microstructure Oxidation Thermal Cycling Carbon-carbon Composites C/c Composites High-temperature 1873 k Multilayer Coatings Room-temperature Resistance
URL查看原文
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/74048
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
B. L.,Hui Zou, Y.,Huang, W. Z.,et al. Oxidation protection of carbon/carbon composites with a plasma-sprayed ZrB2-SiC-Si/Yb2SiO5/LaMgAal(11)O(19) coating during thermal cycling[J]. Journal of the European Ceramic Society,2015,35(7):2017-2025.
APA B. L..,Hui Zou, Y..,Huang, W. Z..,Zhao, S. M..,Chen, X. L..,...&Cao, X. Q..(2015).Oxidation protection of carbon/carbon composites with a plasma-sprayed ZrB2-SiC-Si/Yb2SiO5/LaMgAal(11)O(19) coating during thermal cycling.Journal of the European Ceramic Society,35(7),2017-2025.
MLA B. L.,et al."Oxidation protection of carbon/carbon composites with a plasma-sprayed ZrB2-SiC-Si/Yb2SiO5/LaMgAal(11)O(19) coating during thermal cycling".Journal of the European Ceramic Society 35.7(2015):2017-2025.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[B. L.]'s Articles
[Hui Zou, Y.]'s Articles
[Huang, W. Z.]'s Articles
Baidu academic
Similar articles in Baidu academic
[B. L.]'s Articles
[Hui Zou, Y.]'s Articles
[Huang, W. Z.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[B. L.]'s Articles
[Hui Zou, Y.]'s Articles
[Huang, W. Z.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.