题名: GH3535合金的热变形和热加工图(英文)
作者: 季亚奇;  曲顺德;  韩维新
发表日期: 2015-1-15
摘要: 通过热压缩实验研究GH3535合金在温度区间1000~1200°C和应变速率区间0.01~50 s-1的热变形行为。在实验数据基础上得到合金应力曲线和热加工图,且其激活能为356.3 k J/mol。热加工图分为2个区域,稳定区域发生在所有温度区间和应变速率区间0.01~1 s-1,失稳区域发生在应变速率区间1~50 s-1。显微组织观察表明,完全动态再结晶发生条件为(1150°C,0.01 s-1),(1200°C,0.01 s-1)和(1200°C,0.1 s-1),不同条件下得到的晶粒尺寸不同且有未溶解碳化物。流变失稳区域有局部流变和裂纹出现。
刊名: Transactions of Nonferrous Metals Society of China
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
季亚奇,曲顺德,韩维新. Gh3535合金的热变形和热加工图(英文)[J]. Transactions Of Nonferrous Metals Society Of China,2015(1):88-94.
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [季亚奇]'s Articles
 [曲顺德]'s Articles
 [韩维新]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [季亚奇]‘s Articles
 [曲顺德]‘s Articles
 [韩维新]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2016  中国科学院金属研究所  -Feedback
Powered by CSpace