Characterization of the Corrosion Product Films Formed on the As-Cast and Friction-Stir Processed Ni-Al Bronze in a 3.5 wt% NaCl Solution
Song, Q. N.; Zheng, Y. G.; Ni, D. R.; Ma, Z. Y.; ygzheng@imr.ac.cn
2015
Source PublicationCORROSION
ISSN0010-9312
Volume71Issue:5Pages:606-614
AbstractAn as-cast Ni-Al bronze (NAB) was subjected to friction-stir processing (FSP). The friction-stir processed NAB (FSPed NAB) exhibited better corrosion resistance in a 3.5 wt% sodium chloride solution. The corrosion product films formed on the as-cast and FSPed NAB were characterized by scanning electron microscopy (SEM), x-ray diffraction (XRD), and electron probe micro-analysis (EPMA). Uncorroded phases were retained in the films. The interfaces between these phases and their surrounding corrosion products allowed the chloride ions in and reduced the film protectiveness. For the as-cast NAB, the un-corroded phases were large in size or continuous in structure, resulting in continuous interfaces. Therefore, the film on the as-cast NAB exhibited relatively inferior protectiveness. The films on the as-cast and FSPed NAB were similar in composition with mainly copper chloride hydroxide Cu-2(OH)(3)Cl in the outer layer, and Al2O3 and Cu2O with the incorporation of Fe and Ni in the inner layer. Stability of the films in the flowing condition was also studied and a film damage mechanism was raised. In the flowing condition, the film on the as-cast NAB was damaged by crack formation and expansion, while the film on the FSPed NAB was damaged by thinning.
description.department[song, q. n. ; zheng, y. g.] chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, peoples r china ; [ni, d. r. ; ma, z. y.] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china
KeywordCorrosion Product Film Epma Flowing Condition Friction-stir Processing Ni-al Bronze Sem Xrd
Funding OrganizationNational Natural Science Foundation of China [51131008]
Indexed Bysci
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/74663
Collection中国科学院金属研究所
Corresponding Authorygzheng@imr.ac.cn
Recommended Citation
GB/T 7714
Song, Q. N.,Zheng, Y. G.,Ni, D. R.,et al. Characterization of the Corrosion Product Films Formed on the As-Cast and Friction-Stir Processed Ni-Al Bronze in a 3.5 wt% NaCl Solution[J]. CORROSION,2015,71(5):606-614.
APA Song, Q. N.,Zheng, Y. G.,Ni, D. R.,Ma, Z. Y.,&ygzheng@imr.ac.cn.(2015).Characterization of the Corrosion Product Films Formed on the As-Cast and Friction-Stir Processed Ni-Al Bronze in a 3.5 wt% NaCl Solution.CORROSION,71(5),606-614.
MLA Song, Q. N.,et al."Characterization of the Corrosion Product Films Formed on the As-Cast and Friction-Stir Processed Ni-Al Bronze in a 3.5 wt% NaCl Solution".CORROSION 71.5(2015):606-614.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Song, Q. N.]'s Articles
[Zheng, Y. G.]'s Articles
[Ni, D. R.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Song, Q. N.]'s Articles
[Zheng, Y. G.]'s Articles
[Ni, D. R.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Song, Q. N.]'s Articles
[Zheng, Y. G.]'s Articles
[Ni, D. R.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.