Comparative study of oxidation and interdiffusion behavior of AIP NiCrAlY and sputtered nanocrystalline coatings on a nickel-based single-crystal superalloy | |
Wang, Jinlong; Chen, Minghui; Yang, Lanlan; Zhu, Shenglong; Wang, Fuhui; mhchen@imr.ac.cn | |
2015 | |
发表期刊 | CORROSION SCIENCE
![]() |
ISSN | 0010-938X |
卷号 | 98页码:530-540 |
摘要 | The oxidation and interdiffusin behavior of NiCrAlY and sputtered nanocrystalline coatings on a single-crystal superalloy were studied. Results indicated that the superalloy substrate already possessed a high oxidation resistance. However the spallation resistance of oxide scale was very low. NiCrAlY coating enhanced the spallation resistance to some extent of the superalloy substrate at the expense of elevating oxidation rate and occurrence of severe interdiffusion. Sputtered nanocrystalline coating enhanced substantially the spallation resistance of the superalloy substrate meanwhile avoided elements interdiffusion. Its oxidation rate was lower than the superalloy substrate at 1000 degrees C but a little higher at 1100 degrees C. (C) 2015 Elsevier Ltd. All rights reserved. |
部门归属 | [wang, jinlong ; wang, fuhui] harbin engn univ, corros & protect lab, key lab superlight mat & surface technol, minist educ, harbin 150001, peoples r china ; [wang, jinlong ; chen, minghui ; yang, lanlan ; zhu, shenglong ; wang, fuhui] chinese acad sci, inst met res, lab corros & protect, shenyang 110016, peoples r china |
关键词 | Metal Coatings Superalloys Oxidation |
资助者 | National Natural Science Foundation of China [51471177]; National Basic Research Program of China (973 Program) [2010CB631206]; National Key Basic Research Program of China (973 Program) [2012CB625102] |
收录类别 | sci |
语种 | 英语 |
WOS记录号 | WOS:000359504600054 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.imr.ac.cn/handle/321006/74673 |
专题 | 中国科学院金属研究所 |
通讯作者 | mhchen@imr.ac.cn |
推荐引用方式 GB/T 7714 | Wang, Jinlong,Chen, Minghui,Yang, Lanlan,et al. Comparative study of oxidation and interdiffusion behavior of AIP NiCrAlY and sputtered nanocrystalline coatings on a nickel-based single-crystal superalloy[J]. CORROSION SCIENCE,2015,98:530-540. |
APA | Wang, Jinlong,Chen, Minghui,Yang, Lanlan,Zhu, Shenglong,Wang, Fuhui,&mhchen@imr.ac.cn.(2015).Comparative study of oxidation and interdiffusion behavior of AIP NiCrAlY and sputtered nanocrystalline coatings on a nickel-based single-crystal superalloy.CORROSION SCIENCE,98,530-540. |
MLA | Wang, Jinlong,et al."Comparative study of oxidation and interdiffusion behavior of AIP NiCrAlY and sputtered nanocrystalline coatings on a nickel-based single-crystal superalloy".CORROSION SCIENCE 98(2015):530-540. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论